PBT DURANEX® 3316 CT JAPAN POLYPLASTIC

Unit Price:
$3790 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
11MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.16	%
Density / Specific Gravity		ASTMD792	1.66	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.66	g/cm³
Melt Volume flow Rate	250°C/2.16kg	ISO1133	7.00	cm3/10min
Modeling Shrinkage	MD	ASTMD955	0.30to0.50	%
	Modeling Shrinkage	TD	ISO294-4	0.80to1.3	%
	Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.10to0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	23°C	ASTMD638	9650	Mpa
Tensile Modulus	Tensile Modulus		ISO527-2/1A/1	10700	Mpa
Tensile Strength	Break,23°C	ASTMD638	134	Mpa
Tensile Stress	Break	ISO527-2/1A/5	135	Mpa
Tensile Elongation	Break,23°C	ASTMD638	2.5	%
Tensile Strain	Break	ISO527-2/1A/5	2.5	%
Flexural Modulus	23°C	ISO178	10300	Mpa
Flexural Stress	23°C	ISO178	200	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	220	°C
	Deflection Temperature Under Load?	0.45MPa,Annealed	ASTMD648	221	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	206	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	208	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0MPa,Unannealed	ISO75-2/C	165	°C
Vicat Softening Temperature		ISO306/B50	225	°C
Peak Melting Temperature		ASTMD3418	225	°C
Melting Temperature		ISO11357-3	225	°C
Linear thermal expansion coefficient	MD	ISO11359-2	2.5E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	7.7E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	1E+15	ohms
Volume Resistivity		ASTMD257	2E+16	ohms·cm
Volume Resistivity	Volume Resistivity		IEC60093	1E+15	ohms·cm
Dielectric Strength		ASTMD149	20	KV/mm
Dielectric Strength		IEC60243-1	34	KV/mm
Dielectric Constant	1MHz	ASTMD150	3.50
Relative Permittivity	100Hz	IEC60250	3.60
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	2.90
Dissipation Factor?	1MHz	ASTMD150	0.020
	Dissipation Factor?	100Hz	IEC60250	3.3E-03
	Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.015
Arc Resistance		ASTMD495	106	sec
Comparative Tracking Index		ASTMD3638	250	V
Comparative Tracking Index	Comparative Tracking Index		IEC60112	250	V

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	8.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.5	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	42	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	59	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/1A	7.7	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ISO2039-2	89

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	5VA
Oxygen Index		ISO4589-2	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.