PBT VALOX™ 4631 SABIC INNOVATIVE US
78
- Unit Price:
- $4132 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 26MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Electrical performance Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic display Automotive External Parts
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation,23°C | ISO62 | 0.25 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.070 | % | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ASTMD1238 | 13 | g/10min |
| 250°C/5.0kg | ASTMD1238 | 67 | g/10min | |
| 265°C/5.0kg | ASTMD1238 | 90 | g/10min | |
| 266°C/5.0kg | ASTMD1238 | 90 | g/10min | |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 40.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 65.0 | cm3/10min | |
| Density / Specific Gravity | ASTMD792,ISO1183 | 1.67 | g/cm³ | |
| Modeling Shrinkage | MD | 内部方法 | 0.10到0.30 | % |
| TD | 内部方法 | 0.40到0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strain (Break) | ISO178 | 3.0 | % | |
| Flexural Stress | --7,8 | ISO178 | 200 | Mpa |
| Yield,50.0mmSpan6 | ASTMD790 | 200 | Mpa | |
| Break,50.0mmSpan6 | ASTMD790 | 200 | Mpa | |
| Tensile Strength | Yield5 | ASTMD638 | 130 | Mpa |
| Yield | ISO527-2/5 | 130 | Mpa | |
| Break5 | ASTMD638 | 130 | Mpa | |
| Break | ISO527-2/5 | 130 | Mpa | |
| Tensile Modulus | --4 | ASTMD638 | 11500 | Mpa |
| -- | ISO527-2/1 | 11500 | Mpa | |
| Tensile Elongation | Yield5 | ASTMD638 | 2.0 | % |
| Yield | ISO527-2/5 | 2.0 | % | |
| Break5 | ASTMD638 | 2.0 | % | |
| Break | ISO527-2/5 | 2.0 | % | |
| Flexural Modulus | 50.0mmSpan6 | ASTMD790 | 9000 | Mpa |
| --7 | ISO178 | 9600 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 220 | °C |
| 0.45MPa,Unannealed,100mmSpan12 | ISO75-2/Be | 220 | °C | |
| 0.45MPa,Unannealed,64.0mmSpan13 | ISO75-2/Bf | 220 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 205 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan13 | ISO75-2/Af | 205 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| Linear thermal expansion coefficient | MD:-40to40°C | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| MD:23to80°C | ISO11359-2 | 1.6E-05 | cm/cm/°C | |
| MD:23to150°C | ISO11359-2 | 1.4E-05 | cm/cm/°C | |
| TD:-40to40°C | ISO11359-2 | 8.2E-05 | cm/cm/°C | |
| TD:23to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD:23to150°C | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| Vicat Softening Temperature | -- | ASTMD152514,ISO306/B50,ISO306/B120 | 205 | °C |
| -- | ASTMD152515,ISO306/A5015 | 220 | °C | |
| RTI | UL746 | 140 | °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot-wire Ignition | HWI | UL746 | PLC0 | |
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Dielectric Strength | 0.800mm,in Oil | IEC60243-1 | 27 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 23 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 19 | KV/mm | |
| Comparative Tracking Index | IEC60112 | 250 | V | |
| Dissipation Factor? | 1MHz | ASTMD150,IEC60250 | 0.010 | |
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Dielectric Constant | 1MHz | ASTMD150,IEC60250 | 3.50 | |
| 50Hz | IEC60250 | 3.00 | ||
| 60Hz | IEC60250 | 3.00 | ||
| Volume Resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| High Amp Arc Ignition | HAI | UL746 | PLC3 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 115 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C10 | ISO179/1eU | 55 | kJ/m² |
| -30°C | ISO179/2U | 50 | kJ/m² | |
| 23°C10 | ISO179/1eU,ISO179/2U | 50 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ASTMD4812 | 660 | J/m |
| 23°C | ASTMD4812 | 660 | J/m | |
| -30°C11 | ISO180/1U | 45 | kJ/m² | |
| 23°C11 | ISO180/1U | 45 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C10 | ISO179/1eA | 10 | kJ/m² |
| -30°C | ISO179/2C | 9.0 | kJ/m² | |
| 23°C10 | ISO179/1eA | 10 | kJ/m² | |
| 23°C | ISO179/2C | 11 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 80 | J/m |
| 0°C | ASTMD256 | 80 | J/m | |
| 23°C | ASTMD256 | 80 | J/m | |
| -30°C11 | ISO180/1A | 8.0 | kJ/m² | |
| 0°C11 | ISO180/1A | 8.0 | kJ/m² | |
| 23°C11 | ISO180/1A | 8.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Sale | ISO2039-2 | 118 | |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO4589-2 | 34 | % | |
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filler Content | ASTMD229 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.