Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 1.8 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.8 | % |
Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 33 | g/10min |
Ejection Temperature | | | 170 | °C |
Density / Specific Gravity | | ISO1183 | 1.31 | g/cm³ |
Density / Specific Gravity | | g/cm | ISO 1183 | 1.31 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2 | 20 | % |
Tensile Modulus | | ISO527-2 | 2600 | Mpa |
Tensile Modulus | 0.00 mm, 23 ℃, Injection Molded | MPa | ISO 527-1, -2 | 2600 |
Flexural Strength | 0.00 mm, 23 ℃, 0.0 % | MPa | ISO 178 | 85 |
Tensile Stress | Yield | ISO527-2 | 58.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 4.0 | % |
Flexural Stress | | ISO178 | 85.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | -,6.00 mm | | UL 94 | HB |
Flame Rating | -,3.00 mm | | UL 94 | HB |
Flame Rating | -,1.50 mm | | UL 94 | HB |
Melting Temperature | | ISO11357-3 | 225 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.5 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 4.0 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.75mm | UL94 | HB | |
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
FMVSS Flammability | | FMVSS302 | B | |
Burning Rate | 1.00mm | ISO3795 | 28 | mm/min |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
Odor | | VDA270 | 3.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.