PBT VALOX™ VX5022-1001 SABIC INNOVATIVE US

Unit Price:
$6056 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility High crystallinity Aging resistance Filler: Glass fiber reinf 20% filler by weight
Application Areas:Electronic and electrical engineering application Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density / Specific Gravity		ASTMD792,ISO1183	1.39	g/cm³
Melt Mass-Flow Rate	250°C/2.16kg	ASTMD1238	16	g/10min
	Melt Mass-Flow Rate	265°C/5.0kg	ASTMD1238	50	g/10min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	266°C/5.0kg	ASTMD1238	50	g/10min
Melt Volume flow Rate	250°C/2.16kg	ISO1133	13.0	cm3/10min
	Melt Volume flow Rate	250°C/5.0kg	ISO1133	28.0	cm3/10min
	Melt Volume flow Rate	Melt Volume flow Rate	265°C/5.0kg	ISO1133	40.0	cm3/10min
Modeling Shrinkage	MD1	内部方法	0.30到0.80	%
	Modeling Shrinkage	MD:3.20mm	内部方法	0.30到0.50	%
	Modeling Shrinkage	Modeling Shrinkage	TD2	内部方法	0.50到0.90	%
Moisture Absorption	Saturation,23°C	ISO62	0.10	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.060	%

Mechanical Properties	Test Method	Test Result	Unit
--3	ASTMD638	7300	Mpa
--	ISO527-2/1	7100	Mpa
Yield	ASTMD638	125	Mpa
yield	ISO527-2/5	110	Mpa
Break	ASTMD638	125	Mpa
fracture	ISO527-2/5	110	Mpa
Yield	ASTMD638	3.0	%
yield	ISO527-2/5	3.0	%
Break	ASTMD638	3.0	%
fracture	ISO527-2/5	3.0	%
50.0mm Span	ASTMD790	5800	Mpa
--9	ISO178	6300	Mpa
--10	ISO178	150	Mpa
Yield,50.0mm Span	ASTMD790	145	Mpa
Flexural Strain (Break)	ISO178	3.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
1.8MPa, Unannealed,3.20mm		ASTMD648	120	°C
1.8MPa, Unannealed,64.0mm Span		ISO75-2/Af	120	°C
--		ASTMD1525,ISO306/B50,ISO306/B12024	145	°C
--	--		ASTMD1525,ISO306/A501325	200	°C
Ball PressureTest	125°C	IEC60695-10-2	Pass
Flow:-40 to 40°C		ASTME831	4E-05	cm/cm/°C
Flow:-40 to 40°C	Flow:-40 to 40°C		ISO11359-2	2.5E-05	cm/cm/°C
Flow:23 to 60°C		ISO11359-2	4E-05	cm/cm/°C
Flow:23 to 80°C		ISO11359-2	4E-05	cm/cm/°C
Flow:23 to 150°C		ISO11359-2	2.4E-05	cm/cm/°C
Flow:-40 to 40°C		ASTME831	1E-04	cm/cm/°C
Flow:-40 to 40°C	Flow:-40 to 40°C		ISO11359-2	6.9E-05	cm/cm/°C
Flow:23 to 60°C		ISO11359-2	1E-04	cm/cm/°C
Flow:23 to 80°C		ISO11359-2	1E-04	cm/cm/°C
Flow:23 to 150°C		ISO11359-2	1.1E-04	cm/cm/°C
0.45MPa, Unannealed,3.20mm		ASTMD648	180	°C
0.45MPa, Unannealed,3.20mm Span		ISO75-2/Bf	180	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
0.800mm, in oil		IEC60243-1	31	KV/mm
1.60mm,in Oil		IEC60243-1	28	KV/mm
3.20mm,in Oil		IEC60243-1	16	KV/mm
1MHz		ASTMD150,IEC60250	3.30
50Hz		IEC60250	3.10
60Hz		IEC60250	3.10
100Hz		IEC60250	3.30
1MHz		ASTMD150,IEC60250	0.014
50Hz		IEC60250	1E-03
60Hz		IEC60250	1E-03
100Hz		IEC60250	1E-03
Comparative Tracking Index	--	IEC60112	200	V
Comparative Tracking Index	Comparative Tracking Index	SolutionB	IEC60112	100	V
High Amp Arc Ignition	HAI	UL746	PLC0
Hot-wire Ignition	HWI	UL746	PLC0
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		ASTMD257,IEC60093	>1.0E+15	ohms·cm
0.800mm,inOil		ASTMD149	31	KV/mm
1.60mm,inOil		ASTMD149	28	KV/mm
3.20mm,inOil		ASTMD149	16	KV/mm

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	260°C,1500sec^-1	ISO11443	215	Pa·s

Impact Properties	Test Condition	Test Method	Test Result	Unit
-30°C		ISO179/2C	9.0	kJ/m²
23°C14		ISO179/1eA	6.5	kJ/m²
23°C		ISO179/2C	9.0	kJ/m²
-30°C15		ISO179/1eU	40	kJ/m²
-30°C		ISO179/2U	50	kJ/m²
23°C16		ISO179/1eU	40	kJ/m²
23°C		ISO179/2U	55	kJ/m²
-30°C		ASTMD256	80	J/m
0°C		ASTMD256	80	J/m
23°C		ASTMD256	80	J/m
-30°C13		ISO179/1eA	5.5	kJ/m²
-30°C17		ISO180/1A	6.0	kJ/m²
0°C18		ISO180/1A	7.0	kJ/m²
23°C19		ISO180/1A	7.0	kJ/m²
-30°C		ASTMD4812	650	J/m
23°C		ASTMD4812	650	J/m
-30°C20		ISO180/1U	35	kJ/m²
23°C21		ISO180/1U	40	kJ/m²
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	65.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Sale	ISO2039-2	122
Ball Indentation Hardness	H358/30	ISO2039-1	205	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.60mm,TestingbySABIC	UL94	HB
Glow Wire Flammability Index	1.00mm	IEC60695-2-12	750	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	2.00mm	IEC60695-2-12	850	°C
Oxygen Index		ISO4589-2	23	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
Filler Content		ASTMD229	20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.