PBT VALOX™ 420SEOM-7001 SABIC INNOVATIVE JAPAN
59
- Unit Price:
- $2038 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 200MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | Flow 2 | 内部方法 | 0.10 到 0.50 | % |
Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
Across Flow 2 | 内部方法 | 0.40 到 0.80 | % | |
Across Flow : 3.20 mm | 内部方法 | 0.50 到 1.0 | % | |
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.090 | % |
Equilibrium, 23°C, 50% RH | ISO 62 | 0.070 | % | |
Specific Volume | ASTM D792 | 0.610 | cm³/g | |
Outdoor Suitability | UL 746C | f2 | ||
Melt Mass-Flow Rate | 250°C/5.0 kg | ASTM D1238 | 42 | g/10 min |
Melt Volume flow Rate | 250°C/5.0 kg | ISO 1133 | 29.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flexural Stress | -- | ISO 178 | 180 | Mpa |
Break, 50.0 mm Span 5 | ASTM D790 | 186 | Mpa | |
Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 Wheel | 内部方法 | 22.0 | mg |
Tensile Modulus | -- 3 | ASTM D638 | 12000 | Mpa |
-- | ISO 527-2/1 | 10000 | Mpa | |
Tensile Elongation | Yield 4 | ASTM D638 | 2.0 | % |
Yield | ISO 527-2/5 | 1.9 | % | |
Break 4 | ASTM D638 | 2.0 | % | |
Break | ISO 527-2/5 | 1.9 | % | |
Flexural Modulus | 50.0 mm Span 5 | ASTM D790 | 9800 | Mpa |
-- 6 | ISO 178 | 9500 | Mpa | |
Tensile Strength | Yield 4 | ASTM D638 | 120 | Mpa |
Yield | ISO 527-2/5 | 120 | Mpa | |
Break 4 | ASTM D638 | 120 | Mpa | |
Break | ISO 527-2/5 | 120 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Vicat Softening Temperature | -- | ASTM D152510, ISO 306/B50, ISO 306/B120 | 200 | °C |
-- | ISO 306/A50 | 220 | °C | |
Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 2.5E-5 | cm/cm/°C |
Flow : 23 to 80°C | ISO 11359-2 | 2.5E-5 | cm/cm/°C | |
Across Flow : -40 to 40°C | ASTM E831 | 8.9E-5 | cm/cm/°C | |
Across Flow : -40°C | ISO 11359-2 | 8.9E-5 | cm/cm/°C | |
Across Flow : 23 to 80°C | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
Thermal Conductivity | ISO 8302 | 0.25 | W/m/K | |
RTI | UL 746 | 140 | °C | |
RTI Imp | UL 746 | 130 | °C | |
RTI Elec | UL 746 | 130 | °C | |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 212 | °C |
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Be | 220 | °C | |
1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 200 | °C | |
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Ae | 195 | °C | |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 200 | °C | |
Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Comparative Tracking Index | -- | IEC 60112 | 175 | V |
Solution B | IEC 60112 | 125 | V | |
High Voltage Arc Tracking Rate | UL 746 | PLC 4 | ||
High Amp Arc Ignition | UL 746 | PLC 0 | ||
Arc Resistance | ASTM D495 | PLC 6 | ||
Comparative Tracking Index | UL 746 | PLC 3 | ||
Hot-wire Ignition | UL 746 | PLC 2 | ||
Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 24 | KV/mm |
3.20 mm, in Air | ASTM D149 | 19 | KV/mm | |
0.800 mm, in Oil | IEC 60243-1 | 23 | KV/mm | |
1.60 mm, in Oil | IEC 60243-1 | 22 | KV/mm | |
3.20 mm, in Oil | IEC 60243-1 | 16 | KV/mm | |
Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
Dielectric Constant | 100 Hz | ASTM D150, IEC 60250 | 3.80 | |
1 MHz | ASTM D150 | 3.70 | ||
50 Hz | IEC 60250 | 3.30 | ||
60 Hz | IEC 60250 | 3.30 | ||
1 MHz | IEC 60250 | 3.30 | ||
Volume Resistivity | ASTM D257, IEC 60093 | > 1.0E+15 | ohms·cm | |
Dissipation Factor? | 100 Hz | ASTM D150, IEC 60250 | 2.0E-3 | |
1 MHz | ASTM D150 | 0.020 | ||
50 Hz | IEC 60250 | 1.0E-3 | ||
60 Hz | IEC 60250 | 1.0E-3 | ||
1 MHz | IEC 60250 | 0.010 |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Temperature | 120 | °C | ||
Suggested Max Moisture | 0.020 | % | ||
Processing (Melt) Temp | 255 到 275 | °C | ||
Mold Temperature | 65 到 90 | °C | ||
Drying Time | 3.0 到 4.0 | hr | ||
Suggested Shot Size | 40 到 80 | % | ||
Rear Temperature | 245 到 265 | °C | ||
Middle Temperature | 250 到 270 | °C | ||
Front Temperature | 255 到 275 | °C | ||
Nozzle Temperature | 250 到 270 | °C | ||
Back Pressure | 0.300 到 0.700 | Mpa | ||
Screw Speed | 50 到 80 | rpm | ||
Vent Depth | 0.025 到 0.038 | mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 5.00 | J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 | kJ/m² |
23°C | ISO 179/1eA | 7.0 | kJ/m² | |
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 50 | kJ/m² |
23°C | ISO 179/1eU | 50 | kJ/m² | |
Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 620 | J/m |
-30°C 8 | ISO 180/1U | 45 | kJ/m² | |
23°C 8 | ISO 180/1U | 45 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | R-Scale | ASTM D785 | 119 | |
R -Sale | ISO 2039-2 | 119 | ||
Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 118 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 | °C |
Oxygen Index | ISO 4589-2 | 32 | % | |
Flame Rating | 0.40 mm | UL 94 | V-2 | |
0.71 mm | UL 94 | V-0 | ||
2.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.