PBT Cristin® T841FR-BK851 DUPONT USA
68
- Unit Price:
- $3492 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant Filler: Glass fiber reinf 10% filler by weight
- Application Areas:Electronic and electrical
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MediumDensity | 1.31 | g/cm³ | ||
| Melt Viscosity | 250°C,1000sec^-1 | ISO11443 | 240000 | mPa·s |
| Ejection Temperature | 150 | °C | ||
| SpecificHeatCapacityofMelt | 1970 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.23 | W/m/K | ||
| Modeling Shrinkage | TD | ISO294-4 | 1.2 | % |
| MD | ISO294-4 | 0.70 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2 | 3900 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 70.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 4.7 | % |
| Tensile Creep Modulus | 1hr | ISO899-1 | 3000 | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 2000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 170 | °C |
| 8.0MPa,Unannealed | ISO75-2/C | 66.0 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 180 | °C | |
| Melting Temperature | ISO11357-3 | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+14 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric Strength | IEC60243-1 | 27 | KV/mm | |
| Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.80 | ||
| Dissipation Factor? | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.018 | ||
| Comparative Tracking Index | IEC60112 | 250 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 46 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 0.75mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | V-0 | ||
| Oxygen Index | ISO4589-2 | 30 | % | |
| FMVSS Flammability | FMVSS302 | DNI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.