PBT Cristin® S600F20-NC010 DUPONT USA
86
- Unit Price:
- $4973 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced Good dimensional stabilit Good resistance to chemic
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | -，23C/59RH | % | ISO 62 | 0.2 |
| -，Sat/23C | % | ISO 62 | 0.40 | |
| Saturation,23°C,2.00mm | ISO62 | 0.40 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| Modeling Shrinkage | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.7 | % | |
| -，Across Flow | % | ISO 294-4 | 1.6 | |
| -，Flow | % | ISO 294-4 | 1.7 | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 19 | g/10min |
| MediumDensity | 1.11 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 2110 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K | ||
| Viscosity number | ISO307 | 130 | cm³/g | |
| Density / Specific Gravity | g/cm | ISO 1183 | 1.31 | |
| ISO1183 | 1.31 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | ISO527-2 | 40 | % | |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise | KJ/m | ISO 179 | No Break |
| -，23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | No Break | |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | |
| -，23 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | ||
| Tensile Creep Modulus | 1hr | ISO899-1 | 2600 | Mpa |
| Tensile Strain (Break) | 23 ℃, 50 mm/min | % | ISO 527-1, -2 | |
| Tensile Stress (Yield) | 23 ℃, 50 mm/min | MPa | ISO 527-1, -2 | 58 |
| Tensile Strain (Yield) | 23 ℃, 50 mm/min | % | ISO 527-1, -2 | 7.6 |
| Tensile Strain (Break) | 23 ℃, 50 mm/min | % | ISO 527-1, -2 | |
| Flexural Stress | ISO178 | 85.0 | Mpa | |
| Notched Impact Strength | 23 ℃, Type 1, Notch A | KJ/m | ISO 180 | |
| Tensile Creep Modulus | -，1000h | MPa | ISO 899-1 | 1800 |
| 1000hr | ISO899-1 | 1800 | Mpa | |
| Tensile Stress | Yield | ISO527-2 | 58.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 5.0 | % |
| Tensile Modulus | 23 ℃, 1.0 mm/min | MPa | ISO 527-1, -2 | 2600 |
| ISO527-2 | 2500 | Mpa | ||
| Flexural Modulus | ISO178 | 2200 | Mpa | |
| Flexural Strength | MPa | ISO 178 | 85 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 180 |
| -，1.8 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | ||
| 0.45MPa,Unannealed | ISO75-2/B | 115 | °C | |
| 0.45MPa,Annealed | ISO75-2/B | 180 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 50.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 60.0 | °C | |
| Flame Rating | 1.50 mm | UL94 | HB | |
| 3.00 mm | UL94 | HB | ||
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| MD：55to160°C | ISO11359-2 | 1.9E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 2E-04 | cm/cm/°C | |
| MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Coefficient of Linear Thermal Expansion | 平行Flow ，23 to 55°C (73 to 130°F) | cm/cm/°C | ISO 11359-1, -2 | 0.00013 |
| 垂直Flow ，23 to 55°C (73 to 130°F) | cm/cm/°C | ISO 11359-1, -2 | 0.00013 | |
| PeakCrystallizationTemperature2 | ISO11357-3 | 192 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 175 | °C | |
| Melting Temperature | ISO11357-3 | 225 | °C | |
| Glass Transition Temperature | ISO11357-2 | 55.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.60 | |
| 1MHz | IEC60250 | 3.20 | ||
| Comparative Tracking Index | IEC60112 | 400 | V | |
| Dielectric Strength | IEC60243-1 | 26 | KV/mm | |
| Dissipation Factor? | 100Hz | IEC60250 | 7.9E-04 | |
| 1MHz | IEC60250 | 0.020 | ||
| Surface Resistivity | IEC60093 | 1E+12 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Notched Izod impact strength | 23°C | ISO180/1U | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.0 | kJ/m² |
| 23°C | ISO179/1eA | 5.0 | kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 4.5 | kJ/m² |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | % | ISO 4589-1, -2 | 22 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 22 | % | |
| FMVSS Flammability | FMVSS302 | SE | ||
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Odor3 | VDA270 | 3.00 | ||
| ThermalDesorptionAnalysisofOrganicEmissions4 | VDA278 | 1.00 | µg/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.