PBT Crastin® S620F20 DUPONT BELGIUM
79
- Unit Price:
- $3533 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity
- Application Areas:Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.7 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 19 | g/10min |
| Viscosity number | ISO307 | 130 | cm³/g | |
| Density / Specific Gravity | ISO1183 | 1.31 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO178 | 88.0 | Mpa | |
| Nominal Tensile Strain at Break | ISO527-2 | 30 | % | |
| Tensile Stress | Yield | ISO527-2 | 59.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 8.0 | % |
| Tensile Creep Modulus | 1hr | ISO899-1 | 2600 | Mpa |
| 1000hr | ISO899-1 | 1800 | Mpa | |
| Tensile Modulus | ISO527-2 | 2600 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 0.45MPa,Annealed | ISO75-2/B | 180 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 60.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 60.0 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50 | 175 | °C | |
| Melting Temperature | ISO11357-3 | 225 | °C | |
| Peak Crystallization Temperature | ISO11357-3 | 192 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.80 | |
| 1MHz | IEC60250 | 3.20 | ||
| Comparative Tracking Index | IEC60112 | 600 | V | |
| Dielectric Strength | IEC60243-1 | 26 | KV/mm | |
| Dissipation Factor? | 100Hz | IEC60250 | 2E-03 | |
| 1MHz | IEC60250 | 0.020 | ||
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Density | 1.11 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 2100 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod impact strength | -30°C | ISO180/1U | 70 | kJ/m² |
| 23°C | ISO180/1U | 140 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 | kJ/m² |
| 23°C | ISO179/1eA | 4.5 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 4.0 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS Flammability | FMVSS302 | SE/NBR | ||
| UL flame retardant rating | 0.8mm | UL94,IEC60695-11-10,-20 | HB | |
| 1.5mm | UL94,IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 22 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.