PBT Cristin® S620F20 DUPONT USA

Unit Price:
$3528 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
43.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.6	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.7	%
Moisture Absorption	Saturation,23°C,2.00mm	ISO62	0.40	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
Melt Mass-Flow Rate	250°C/2.16kg	ISO1133	19	g/10min
Viscosity number		ISO307	130	cm³/g
Density / Specific Gravity		ISO1183	1.31	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	88.0	Mpa
Nominal Tensile Strain at Break		ISO527-2	30	%
Tensile Stress	Yield	ISO527-2	59.0	Mpa
Tensile Strain	Yield	ISO527-2	8.0	%
Tensile Creep Modulus	1hr	ISO899-1	2600	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1000hr	ISO899-1	1800	Mpa
Tensile Modulus		ISO527-2	2600	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	145	°C
	Deflection Temperature Under Load?	0.45MPa,Annealed	ISO75-2/B	180	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	60.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Annealed	ISO75-2/A	60.0	°C
Linear thermal expansion coefficient	MD	ISO11359-2	1.3E-04	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1.3E-04	cm/cm/°C
Vicat Softening Temperature		ISO306/B50	175	°C
Melting Temperature		ISO11357-3	225	°C
Peak Crystallization Temperature		ISO11357-3	192	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100Hz	IEC60250	3.80
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.20
Comparative Tracking Index		IEC60112	600	V
Dielectric Strength		IEC60243-1	26	KV/mm
Dissipation Factor?	100Hz	IEC60250	2E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.020
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm

Fill Analysis	Test Result	Unit
Melt Density	1.11	g/cm³
Ejection Temperature	170	°C
SpecificHeatCapacityofMelt	2100	J/kg/°C
ThermalConductivityofMelt	0.21	W/m/K

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	-30°C	ISO180/1U	70	kJ/m²
Notched Izod impact strength	Notched Izod impact strength	23°C	ISO180/1U	140	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	无断裂
Charpy Notched Impact Strength	-30°C	ISO179/1eA	3.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	4.5	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	5.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	4.0	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
FMVSS Flammability		FMVSS302	SE/NBR
UL flame retardant rating	0.8mm	UL94,IEC60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL94,IEC60695-11-10,-20	HB
Oxygen Index		ISO4589-2	22	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.