Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 1.9 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.9 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.40 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Apparent Density | | | 0.70到0.80 | g/cm³ |
Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 16.0 | cm3/10min |
Viscosity Number | | ISO307 | 115 | cm³/g |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Creep Modulus | 1000hr | ISO899-1 | 1300 | Mpa |
Flexural Stress | | ISO178 | 100 | Mpa |
Tensile Stress | Break | ISO527-2 | 48.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 6.0 | % |
Tensile Modulus | | ISO527-2 | 3500 | Mpa |
Flexural Modulus | | ISO178 | 3400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 170 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
Linear thermal expansion coefficient | MD:23to80°C | ISO11359-2 | 8.0E-5到9.0E-5 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 223 | °C |
Specific Heat | | | 1150 | J/kg/°C |
Thermal Conductivity | | DIN52612 | 0.27 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 1MHz | IEC60250 | 3.70 | |
Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
Comparative Tracking Index | SolutionA | IEC60112 | 250 | V |
Comparative Tracking Index | SolutionB | IEC60112 | 125 | V |
Dissipation Factor? | 100Hz | IEC60250 | 0.012 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.019 | |
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 26 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 35 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H358/30 | ISO2039-1 | 150 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flammability level | 0.75mm | IEC60695-11-10,-20 | HB | |
Flammability level | 1.6mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.