PBT Toraycon® 5201-X10-BK TORAY JAPAN

102

Unit Price:
$3188 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electrical field Electronic field Automotive sector
Color:--
Grade:Impact resistant grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm2	内部方法	2.5	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	2.0	%
Water absorption rate	23°C,24hr	ISO62	0.080	%
Water absorption rate	Water absorption rate	23℃·24hr	ASTM D-570	0.08	%
Film plastic shrinkage	80×80×3板材		2.0-2.5	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Fracture tensile elongation	23℃	ASTM D-638	>150	%
IZOD impact strength (1/8 hour width)	Unnotched，23℃	ASTM D-256	不破裂	kg.cm/cm
	IZOD impact strength (1/8 hour width)	Unnotched，-40℃	ASTM D-256	160	kg.cm/cm
		IZOD impact strength (1/8 hour width)	Notched，23℃	ASTM D-256	6.4	kg.cm/cm
		IZOD impact strength (1/8 hour width)	IZOD impact strength (1/8 hour width)	Notched，-40℃	ASTM D-256	5.0	kg.cm/cm
Under load	4.6kg/cm	ASTM D-648	154	°C
Under load	Under load	18.6kg.cm	ASTM D-648	56	°C
Tensile stress	Yield,23°C	ISO527-2	50.0	Mpa
Tensile strain	Break,23°C	ISO527-2	50	%
Bending stress	23°C	ISO178	80.0	Mpa
Tensile modulus	23°C	ISO527-2	2600	Mpa
tensile strength	23℃	ASTM D-638	490	kg/cm
Rockwell hardness	23℃	ASTM D-785	59	M标度
Rockwell hardness	Rockwell hardness	23℃	ASTM D-785	108
Bending modulus	23℃	ASTM D-790	23	kg/cm
Bending modulus	Bending modulus	23°C	ISO178	2400	Mpa
bending strength	23℃	ASTM D-790	770	kg/cm

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	150	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	55.0	°C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO11359-2	1.4E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor 4	23°C,50Hz	IEC60250	2E-03
Dissipation factor 4	Dissipation factor 4	23°C,1MHz	IEC60250	0.020
Arc resistance 5		IEC60950	130	sec
Volume resistivity		IEC60093	4E+16	ohms·cm
Dielectric strength		IEC60243-1	19	KV/mm
Compared to the anti leakage trace index	CTI	UL746	PLC0
Dielectric constant 5	23°C,50Hz	IEC60250	3.40
Dielectric constant 5	Dielectric constant 5	23°C,1kHz	IEC60250	3.50

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	290	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale,23°C	ISO2039-2	70

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength6	250°C,1.00mm	内部方法	8.70	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.