PBT 3300-2 CELANESE USA
111
- Unit Price:
- $3654 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced 30% enhancement
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 0.3-0.5 | % |
| Across Flow | ISO 294-4 | 0.7-0.9 | % | |
| Water absorption rate | 23℃,Saturation | ISO 62 | 0.4 | % |
| 23℃,50%相对湿度 | ISO 62 | 0.2 | % | |
| Melt volume ratio | ISO 1133 | 17 | CM | |
| Density/specific gravity | ISO 1183 | 1530 | kg/m |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 7.5 | KJ/m |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 8.5 | KJ/m |
| -30℃ | ISO 179/1eA | 8.5 | KJ/m | |
| Charpy impact strength | 23℃ | ISO 179/1eU | 46 | KJ/m |
| -30℃ | ISO 179/1eU | 45 | KJ/m | |
| elongation at break | 5mm/min | ISO 527-2/1A | 2.5 | % |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 9200 | Mpa |
| tensile strength | 5mm/min | ISO 527-2/1A | 130 | Mpa |
| Rockwell hardness | ISO 2039-2 | 90 | M | |
| Bending modulus | 23℃ | ISO 178 | 9700 | Mpa |
| bending strength | 23℃ | ISO 178 | 210 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45Mpa | ISO 75-1/-2 | 225 | °C |
| 8.0Mpa | ISO 75-1/-2 | 150 | °C | |
| 1.8Mpa | ISO 75-1/-2 | 205 | °C | |
| Flame retardancy | UL94 | HB | ||
| Melting temperature | ISO 11357-1,-2,-3 | 225 | °C | |
| Vicat softening temperature | ISO 306 | 220 | °C | |
| Coefficient of linear expansion | Across Flow | ISO 11359-2 | 0.25 | E-4/℃ |
| Across Flow | ISO 11359-2 | 1 | E-4/℃ | |
| Glass transition temperature | ISO 11357-1,-2,-3 | 60 | °C | |
| Oxygen index | ISO 4589 | 20 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative resistivity | 1MHz | IEC 60250 | 4.1 | |
| 100Hz | IEC 6250 | 4.5 | ||
| Relative Trace Index | IEC 60112 | 425 | ||
| Dielectric dissipation factor | 100Hz | IEC 60250 | 22 | E-4 |
| 1MHz | IEC 60250 | 160 | E-4 | |
| Dielectric strength | IEC 60243-1 | 31 | KV/mm | |
| Surface resistivity | IEC 60093 | ＞1E15 | Ohm | |
| Volume resistivity | IEC 60093 | ＞1E13 | ohm.m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.