PBT Toraycon® 1100M TORAY JAPAN
96
- Unit Price:
- $3351 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant High temperature resistan
- Application Areas:PBT board Electrical tools Electrical field Electronic field Household appliances Household appliances Fitness equipment Profile Lighting fixtures
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.315 | ||
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 59 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume ratio | cm | ISO 1133 | 59 | |
| Melt mass flow rate | 250°C/1.0kg | ISO1133 | 31 | g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 59.0 | cm3/10min |
| Viscosity value 2 | 0.5%OCP | 内部方法 | 85.0 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield | ASTMD638 | 57.0 | Mpa |
| Tensile stress | ISO527-2 | 60.0 | Mpa | |
| elongation | Break | ASTMD638 | 27 | % |
| Tensile strain | Break | ISO527-2 | 32 | % |
| Bending modulus | ASTMD790 | 2500 | Mpa | |
| ISO178 | 2500 | Mpa | ||
| bending strength | ASTMD790 | 84.0 | Mpa | |
| Bending stress | ISO178 | 87.0 | Mpa | |
| tensile strength | MPa | ISO 527-1/-2 | ||
| elongation | % | ISO 527-1/-2 | ||
| bending strength | MPa | ISO 178 | 87 | |
| Bending modulus | Gpa | ISO 178 | 2.5 | |
| Charpy notch impact strength | KJ/m | ISO 179 | ||
| elongation at break | ASTM D638/ISO 527 | 32 | % | |
| elongation | ASTM D638/ISO 527 | 32 | % | |
| Bending modulus | ASTM D790/ISO 178 | 2.5 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 87 | kg/cm²(MPa)[Lb/in²] | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 4.4 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardancy | UL94 | HB | ||
| melting point | 224 | ℃（℉） | ||
| Melting temperature | 224 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.