PBT VALOX™ 855-1001 SABIC INNOVATIVE US

Unit Price:
$3527 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Excellent appearance Glass fiber reinforced
Application Areas:Electrical field Electrical appliances Electronic field Electronic display Construction field Medical supplies Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 1.50 to 3.20 mm	内部方法	0.40 到 0.60	%
	Modeling Shrinkage	Flow : 3.20 to 4.60 mm	内部方法	0.60 到 0.90	%
		Modeling Shrinkage	Across Flow : 1.50 to 3.20 mm	内部方法	0.50 到 0.80	%
		Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 to 4.60 mm	内部方法	0.80 到 1.1	%
Moisture Absorption	24 hr	ASTM D570	0.060	%
Melt Mass-Flow Rate	266°C/5.0 kg	ASTM D1238	79	g/10 min
Specific Volume		ASTM D792	0.650	cm³/g

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	50.0 mm Span	ASTM D790	5000	Mpa
Flexural Strength	Break, 50.0 mm Span	ASTM D790	143	Mpa
Tensile Strength	Break	ASTM D638	95.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	125	°C
RTI Imp		UL 746	110	°C
RTI Elec		UL 746	125	°C
Coefficient of Linear Thermal Expansion (Flow)	-40 to 40°C	ASTM E831	4.0E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion (Flow)	Coefficient of Linear Thermal Expansion (Flow)	60 to 138°C	ASTM E831	6.1E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	204	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	187	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 0
High Amp Arc Ignition		UL 746	PLC 4
Dielectric Constant	100 Hz	ASTM D150	3.50
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.30
Volume Resistivity		ASTM D257	1.0E+13	ohms·cm
Dissipation Factor?	100 Hz	ASTM D150	1.0E-3
Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.013
Dielectric Strength	1.60 mm, in Oil	ASTM D149	24	KV/mm
Dielectric Strength	Dielectric Strength	3.20 mm, in Air	ASTM D149	20	KV/mm
High Voltage Arc Tracking Rate		UL 746	PLC 4
Arc Resistance		ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	250 到 265	°C
Mold Temperature	65 到 90	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	240 到 255	°C
Middle Temperature	245 到 260	°C
Front Temperature	250 到 265	°C
Nozzle Temperature	245 到 260	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	50 到 80	rpm
Vent Depth	0.025 到 0.038	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	350	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	119

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.