Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | | ASTMD792 | 1.53 | g/cm³ |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.30to0.70 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.60to0.90 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ASTMD638 | 3520 | Mpa |
Tensile Strength | Yield | ASTMD638 | 89.6 | Mpa |
Tensile Strength | Break | ASTMD638 | 91.0 | Mpa |
Tensile Elongation | Yield | ASTMD638 | 2.4 | % |
Tensile Elongation | Break | ASTMD638 | 2.5 | % |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 4960 | Mpa |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 138 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 219 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 205 | °C |
RTIElec | | UL746 | 130 | °C |
Evolution Calendar intelligent importer | | UL746 | 130 | °C |
RTIStr | | UL746 | 130 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Arc Resistance | | ASTMD495 | PLC5 | |
Comparative Tracking Index | CTI | UL746 | PLC2 | |
High Amp Arc Ignition | HAI | UL746 | PLC0 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 | |
Hot-wire Ignition | HWI | UL746 | PLC0 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C | ASTMD256 | 43 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD4812 | 480 | J/m |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.75mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.