Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:270°C,2.00mm2 | ISO294-4 | 0.90 | % |
Modeling Shrinkage | TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.20 | % |
Modeling Shrinkage | MD:270°C,2.00mm2 | ISO294-4 | 0.30 | % |
Modeling Shrinkage | MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.10 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.10 | % |
Apparent Density | | ISO60 | 0.80 | g/cm³ |
Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 30.0 | cm3/10min |
parent Viscosity | 降低的粘度 | ISO1628 | 91.0 | ml/g |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strain | 23°C | | 3.0 | % |
Tensile Strength | Break,23°C | ASTMD638 | 123 | Mpa |
Flexural Stress | 23°C | ISO178 | 230 | Mpa |
Flexural Modulus | 23°C | ISO178/A | 10300 | Mpa |
Tensile Stress | Break,23°C | ISO527-2/5 | 145 | Mpa |
Tensile Strain | Break,23°C | ISO527-2/5 | 2.8 | % |
Tensile Creep Modulus | 1hr | ISO899-1 | 10000 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 8500 | Mpa |
Tensile Modulus | 23°C | ASTMD638 | 9980 | Mpa |
Tensile Modulus | 23°C | ISO527-2/1 | 10400 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 2.5 | % |
Flexural Modulus | 23°C | ASTMD790 | 8550 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 207 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 200 | °C |
RTIElec | | UL746 | 140 | °C |
Evolution Calendar intelligent importer | | UL746 | 125 | °C |
RTIStr | | UL746 | 140 | °C |
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 3E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:23to55°C | ISO11359-2 | 6E-05 | cm/cm/°C |
Vicat Softening Temperature | | ISO306/B120 | 205 | °C |
Thermal Conductivity | 23°C | ISO8302 | 0.27 | W/m/K |
Melting Temperature | | ISO11357-3 | 225to250 | °C |
Temperature Index | 介电强度 | IEC60216 | 155 | |
Temperature Index | 拉伸冲击强度 | IEC60216 | 140 | |
Temperature Index | 抗张强度 | IEC60216 | 155 | |
Half Interval | --8 | IEC60216 | 13.5 | °C |
Half Interval | --9 | IEC60216 | 10.2 | °C |
Half Interval | --10 | IEC60216 | 10.2 | °C |
Ball PressureTest | 220°C | IEC60695-10-2 | Pass | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
Relative Permittivity | 23°C,1MHz | IEC60250 | 3.80 | |
Comparative Tracking Index | SolutionA | IEC60112 | 250 | V |
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 27 | KV/mm |
Film | Test Condition | Test Method | Test Result | Unit |
---|
FilmPunctureEnergy6 | | ISO6603-2 | 2.10 | J |
Film Puncture Force | | ISO6603-2 | 650 | N |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
Notched Izod impact strength | 23°C | ISO180/1U | 55 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 55 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 65 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 200 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 21 | % |
UL flame retardant rating | 0.8mm | UL94 | HB | |
UL flame retardant rating | 1.6mm | UL94 | HB | |
Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 750 | °C |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
ElectrolyticalCorrosion | | IEC60426 | A1 | |
ISO Shortname | | ISO7792 | PBT+PET,GHLMR,09-100,GF30 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.