PBT Ultradur® B 4406 BASF GERMANY

Unit Price:
$3867 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
46.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electrical components switch Connector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1450
Moisture Absorption 23℃/24H		ASTM D570/ISO 62	0.4	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.18mm		0.15	%
Moisture Absorption	Saturation	ASTMD570	0.40	%
	Moisture Absorption	Saturation,23°C	ISO62	0.40	%
		Moisture Absorption	Equilibrium,50%RH	ASTMD570	0.25	%
		Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.25	%
parent Viscosity	降低的粘度	ISO1628	122.0	ml/g
Melt Volume flow Rate	250°C/2.16kg	ISO1133	30.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield,23°C	ASTMD638	65.0	Mpa
Tensile Modulus		ASTM D638/ISO 527	3000	kg/cm²(MPa)[Lb/in²]
Tensile Modulus	Tensile Modulus	23°C	ISO527-2	3000	Mpa
Tensile Elongation	Yield,23°C	ASTMD638	3.9	%
Tensile Stress	Yield,23°C	ISO527-2	65.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2	3.9	%
Tensile Creep Modulus	1hr	ISO899-1	1800	Mpa
Nominal Tensile Strain at Break	-40°C	ISO527-2	3.3	%
Nominal Tensile Strain at Break	Nominal Tensile Strain at Break	23°C	ISO527-2	3.5	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD	ASTME831	9E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD		5.5E-05	cm/cm/°C
Peak Melting Temperature		ASTMD3418	223	°C
RTIElec	0.75mm	UL746	125	°C
	RTIElec	1.5mm	UL746	125	°C
	RTIElec	RTIElec	3.0mm	UL746	125	°C
Evolution Calendar intelligent importer	0.75mm	UL746	130	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	130	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	130	°C
RTIStr	0.75mm	UL746	140	°C
	RTIStr	1.5mm	UL746	140	°C
	RTIStr	RTIStr	3.0mm	UL746	140	°C
Burning Rate		UL94	V-0
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	165	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	170	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	80.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	60.0	°C
Linear expansion coefficient		ASTM D696/ISO 11359	1500	mm/mm.℃
Melting temperature (DSC)		ISO3146	223	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	1E+13	ohms
Dielectric Constant	100Hz	IEC60250	3.30
Dielectric Constant	Dielectric Constant	1MHz	IEC60250	3.30
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Volume Resistivity	Volume Resistivity		ASTM D257/IEC 60093	1E 14	Ω.cm
Dissipation Factor?	100Hz	IEC60250	0.011
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.017
Comparative Tracking Index		IEC60112	250	V
Volume Resistivity	1.50mm	ASTMD257	>1.0E+15	ohms·cm
SurfaceResistivity	1.50mm	ASTMD257	1E+13	ohms

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179	50	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40mm	UL94	V-0
	UL flame retardant rating	0.75mm	UL94	V-0
		UL flame retardant rating	1.5mm	UL94	V-0
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.