PBT CELANEX® 3216 CELANESE USA

Unit Price:
$4104 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant
Application Areas:Connector
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	0.40to0.60	%
	Modeling Shrinkage	TD	ISO294-4	1.1	%
	Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.30to0.60	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.17	%
Melt Volume flow Rate	250°C/2.16kg	ISO1133	9.00	cm3/10min
Density / Specific Gravity		ASTMD792	1.54	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.54	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Break,23°C	ASTMD638	100	Mpa
Flexural Stress	23°C	ISO178	155	Mpa
Tensile Stress	Break	ISO527-2/1A/5	100	Mpa
Tensile Strain	Break	ISO527-2/1A/5	3.0	%
Tensile Modulus		ISO527-2/1A/1	6700	Mpa
Tensile Elongation	Break,23°C	ASTMD638	4.0	%
Flexural Modulus	23°C	ISO178	6000	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	217	°C
	Deflection Temperature Under Load?	0.45MPa,Annealed	ASTMD648	213	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	185	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	200	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0MPa,Unannealed	ISO75-2/C	95.0	°C
Linear thermal expansion coefficient	MD	ISO11359-2	3.6E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1E-04	cm/cm/°C
Vicat Softening Temperature		ISO306/B50	206	°C
Glass Transition Temperature		ISO11357-2	60.0	°C
Peak Melting Temperature		ASTMD3418	225	°C
Melting Temperature		ISO11357-3	225	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100Hz	IEC60250	3.70
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.50
Comparative Tracking Index		ASTMD3638	250	V
Comparative Tracking Index	Comparative Tracking Index		IEC60112	250	V
Dielectric Strength		ASTMD149	26	KV/mm
Dissipation Factor?	1MHz	ASTMD150	0.010
	Dissipation Factor?	100Hz	IEC60250	3.3E-03
	Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.016
Dielectric Strength		IEC60243-1	30	KV/mm
Surface Resistivity		IEC60093	1E+15	ohms
Dielectric Constant	1MHz	ASTMD150	3.20
Arc Resistance		ASTMD495	79.0	sec
Volume Resistivity		IEC60093	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity		ASTMD257	2E+16	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	28	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	28	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	6.0	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/1A	5.5	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ISO2039-2	87

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Oxygen Index		ISO4589-2	27to32	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.