Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.54 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
tensile strength | --- | ASTM D-638 | 112 | Mpa |
Notched Izod Impact Strength | Notched,--- | ASTM D-256 | 58 | J/m |
Notched Izod Impact Strength | 反Notched侧,--- | ASTM D-256 | 440 | J/m |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 3.5 | % |
Tensile Strength | | ASTM D638/ISO 527 | 112 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790/ISO 178 | 6080 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | --- | ASTM D-790 | 6080 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 166 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | --- | ASTM D-790 | 166 | Mpa |
Elongation rate | --- | ASTM D-638 | 3.5 | % |
Charpy impact strength | | ASTM D256/ISO 179 | 58 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 208 | ℃(℉) |
Deflection Temperature Under Load? | 1.82MPa | ASTM D-648 | 208 | °C |
Linear expansion coefficient | --- | --- | 2-7 | ×10-5/℃ |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 2-7 | mm/mm.℃ |
Flame retardancy | --- | UL 94 | V-0 | --- |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Insulation failure strength | 短时:3mmt | ASTM D-149 | 20 | MV/m |
Volume Resistivity | 3mmt | ASTM D-257 | 2×1016 | Ω.cm |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | --- | ASTM D-792 | 1.54 | --- |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Arc Resistance | *2 | --- | 250 | V |
Surface Resistivity | --- | --- | 3×1016 | Ω |
Arc Resistance | *2 | --- | 70 | S |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.