PBT DURANEX® 3300H JAPAN POLYPLASTIC

105

Unit Price:
$3938 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High toughness
Application Areas:Electrical applications Electronic and electrical
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.53

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	23°C,24hr	ISO62	0.10	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress		ISO527-2	140	Mpa
Tensile strain	Break	ISO527-2	2.4	%
tensile strength		ASTM D638/ISO 527	140	kg/cm²(MPa)[Lb/in²]
	tensile strength		ASTM D527-1,2	140	Mpa
	tensile strength	tensile strength		ASTM D-638	132	Mpa
elongation		ASTM D-638	2.5	%
Bending modulus		ASTM D178	9000	Mpa
	Bending modulus		ASTM D-790	9120	Mpa
		Bending modulus		ASTM D790/ISO 178	9000	kg/cm²(MPa)[Lb/in²]
		Bending modulus	Bending modulus		ISO178	9000	Mpa
bending strength		ASTM D790/ISO 178	215	kg/cm²(MPa)[Lb/in²]
	bending strength		ASTM D-790	210	Mpa
	bending strength	bending strength		ASTM D178	215	Mpa
Bending stress		ISO178	215	Mpa
Charpy notch impact strength		ASTM D179/1eA	11.4	kJ/m²
IZOD impact strength (with notch)	Notched侧	ASTM D-256	93	J/m
IZOD impact strength (with notch)	IZOD impact strength (with notch)	反Notched侧	ASTM D-256	530	J/m
Tensile failure strain		ASTM D527-1,2	2.4	%
Tensile elongation at break (elongation at break)		ASTM D638/ISO 527	2.4	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Flame retardancy		UL94	HB
Flame retardancy	Flame retardancy		UL 94	HB
Linear coefficient of thermal expansion	MD：23to55°C	内部方法	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	内部方法	9E-05	cm/cm/°C
Combustibility (rate)		UL94	相当于 HB
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	210	°C
	Hot deformation temperature	1.8Mpa	ASTM D75-1,2	210	°C
	Hot deformation temperature	Hot deformation temperature	1.82MPa	ASTM D-648	213	°C
Linear expansion coefficient (room temperature)			2-7

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity	3mmt	ASTM D-257	5×10	Ω.cm
Dielectric breakdown strength	2mmt	ASTM D-149	23	MV/m
Dielectric strength	3.00mm	IEC60243-1	24	KV/mm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ISO2039-2	100

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ColourNumber			EF2001

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.