PBT DURANEX® 2002 JAPAN POLYPLASTIC

100

Unit Price:
$3356 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
47.3MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Good flexibility Glass fiber reinforced Friction resistance
Application Areas:Electrical field Electronic field
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	792

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	23°C,24hr	ISO62	0.20	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.19	%
Melt Volume flow Rate	250°C/2.16kg	ISO1133	18.0	cm3/10min
Flow		ASTMD955	1.8到2.0	%
Vertical flow direction		ISO294-4	1.8到2.0	%
Flow		ISO294-4	1.8到2.0	%
Melt Mass-Flow Rate		ASTMD1238	20	g/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	95.0	Mpa
Flexural Stress	Flexural Stress	23°C	ISO178	80.0	Mpa
Nominal Tensile Strain at Break		ISO527-2	12	%
Nominal Tensile Strain at Break	Nominal Tensile Strain at Break		ISO527-2/1A/50	>50	%
Tensile Stress (50%)		ISO527-2/1A/50	30.0	Mpa
Break,23℃		ASTMD638	200	%
Charpy Notched Impact Strength		ISO 179/1eA	3.2	kJ/m²
屈服,-40°C		ASTMD638	7.2	%
屈服,-40°C	屈服,-40°C		ASTMD638	101	Mpa
屈服,0°C		ASTMD638	75.8	Mpa
屈服,0°C	屈服,0°C		ASTMD638	4.4	%
Field, 23°C		ASTMD638	3.2	%
Field, 23°C	Field, 23°C		ASTMD638	55.8	Mpa
屈服,80°C		ASTMD638	24.8	Mpa
屈服,80°C	屈服,80°C		ASTMD638	17	%
屈服,121°C		ASTMD638	23	%
屈服,121°C	屈服,121°C		ASTMD638	17.9	Mpa
yield		ISO527-2/1A/50	60.0	Mpa
yield	yield		ISO527-2/1A/50	4.0	%
fracture		ISO527-2/1A/50	220	%
fracture	fracture		ISO527-2/1A/50	35.0	Mpa
Tensile Stress		ISO527-2	57.0	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	>200	%
Tensile Strength		ASTM D638/ISO 527	51	kg/cm²(MPa)[Lb/in²]
	Tensile Strength		ASTM D-638	51	Mpa
	Tensile Strength	Tensile Strength		ISO 527-1/-2	57	Mpa
Tensile Elongation		ASTM D-638	>200	%
Flexural Modulus		ASTM D790/ISO 178	2540	kg/cm²(MPa)[Lb/in²]
	Flexural Modulus	23°C	ISO178	2500	Mpa
		Flexural Modulus		ASTM D-790	2540	Mpa
			Flexural Modulus		ISO 178	3100	Mpa
			Flexural Modulus	Flexural Modulus		ISO178	3100	Mpa
Flexural Strength		ISO 178	95	Mpa
	Flexural Strength		ASTM D790/ISO 178	85	kg/cm²(MPa)[Lb/in²]
	Flexural Strength	Flexural Strength		ASTM D-790	85	Mpa
Izod Impact Strength		ASTM D-256	34	J/m
Izod notch impact strength		ASTM D256/ISO 179	34	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
0.45MPa, Unannealed		ASTMD648	160	°C
0.45MPa, Unannealed	0.45MPa, Unannealed		ISO75-2/B	150	°C
1.8MPa, Unannealed		ASTMD648,ISO75-2/A	55.0	°C
Glass Transition Temperature		ISO11357-2	60.0	°C
Vicat Softening Temperature		ISO306/B50	190	°C
Flame retardancy		UL 94	HB
Flame retardancy	Flame retardancy		UL94	HB
Linear thermal expansion coefficient	MD	ISO11359-2	1.1E-04	cm/cm/°C
	Linear thermal expansion coefficient	TD	ISO11359-2	1.4E-04	cm/cm/°C
		Linear thermal expansion coefficient	MD：23to55°C	内部方法	9E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	内部方法	9E-05	cm/cm/°C
Melting temperature		ISO11357-3,ASTMD3418	225	°C
Deflection Temperature Under Load?	1.8Mpa	ISO 75-1/-2	80	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	80.0	°C
		Deflection Temperature Under Load?		ASTM D648/ISO 75	70	℃（℉）
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.82Mpa	ASTM D-648	70	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	1E+15	ohms
Dissipation Factor?	100Hz	IEC60250	1.4E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.022
Comparative Tracking Index		IEC60112	600	V
Dielectric Strength	3.00mm	IEC60243-1	17	KV/mm
1MHz		IEC60250	3.50
1MHz	1MHz		ASTMD150	3.20
100Hz		IEC60250	4.00
--		ASTMD257	1E+16	ohms·cm
	--		IEC60093	1E+15	ohms·cm
	--	--		IEC60243-1	23	KV/mm
--1		ASTMD149	17	KV/mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	190	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ISO2039-2	85
Rockwell Hardness	Rockwell Hardness	M-Sale	ISO2039-2	78

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.710mm	UL94	HB
UL flame retardant rating	UL flame retardant rating		UL94	HB
Oxygen Index		ISO4589-2	22	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
Color Number			EF2001/ED3002

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.