PBT Toraycon® 5101G-30U TORAY JAPAN

111

Unit Price:
$3443 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance Fast forming cycle
Application Areas:Electrical components Automotive Applications
Color:--
Grade:Enhanced level

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	23℃,24hr	ASTM D570	0.07	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO62	0.070	%
Shrinkage rate	TD:3.00mm2	内部方法	1.0	%
Shrinkage rate	Shrinkage rate	MD:3.00mm3	内部方法	0.40	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Friction coefficient 4			0.19
Friction coefficient vs. Metal5		SuzukiMethod	0.15
friction coefficient	-，对金属	ASTM D1894	0.15
friction coefficient	friction coefficient	-，对本身	ASTM D1894	0.19
Tensile stress	23°C	ISO527-2	130	Mpa
Tensile strain	Break,23°C	ISO527-2	4.0	%
Bending stress	23°C	ISO178	205	Mpa
IZOD notch impact strength	Notched，23℃	ASTM D256	145	J/m
IZOD notch impact strength	IZOD notch impact strength	Unnotched，23℃	ASTM D256	85	KJ/m
Tensile modulus	23°C	ISO527-2	8500	Mpa
tensile strength	23℃	ASTM D638	130	Mpa
elongation	23℃	ASTM D638	5	%
Rockwell hardness		ASTM D785	89	M
Bending modulus	23℃	ASTM D790	7.0	GPa
Bending modulus	Bending modulus	23°C	ISO178	8000	Mpa
bending strength	23℃	ASTM D790	185	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	-，0.45MPa	ASTM D648	225	°C
	Hot deformation temperature	-，1.82Mpa	ASTM D648	215	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	220	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	205	°C
Coefficient of linear expansion		ASTM D696	2.5
Linear coefficient of thermal expansion	MD：-30to100°C	ISO11359-2	4.2E-05	cm/cm/°C
Flame retardancy		UL94	HB

Electrical performance	Test Condition	Test Method	Test Result	Unit
Tangent value of dielectric loss	-，50Hz	ASTM D150	0.002
Tangent value of dielectric loss	Tangent value of dielectric loss	-，10	ASTM D150	0.02
Dissipation factor 6	23°C,50Hz	IEC60250	2E-03
Dissipation factor 6	Dissipation factor 6	23°C,1MHz	IEC60250	0.020
Arc resistance 7		IEC60950	130	sec
Dielectric constant 6	23°C,50Hz	IEC60250	3.90
Dielectric constant 6	Dielectric constant 6	23°C,1kHz	IEC60250	3.70
Arc resistance coefficient		ASTM D495	130	S
Voltage endurance		ASTM D149	31	MV/m
Dielectric constant	-，50Hz	ASTM D150	3.9
Dielectric constant	Dielectric constant	-，10	ASTM D150	3.7
Volume resistivity		ASTM D257	5.0
Volume resistivity	Volume resistivity		IEC60093	1E+17	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	65	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale,23°C	ISO2039-2	60

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength8	250°C,1.00mm	内部方法	6.70	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.