PBT Toraycon® 5101G-15 TORAY JAPAN

107

Unit Price:
$2935 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
40.2MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance Fast forming cycle
Application Areas:Electrical components Automotive Applications
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.36
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.07	%

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	23℃,24hr	ASTM D570	0.07	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO62	0.070	%
Shrinkage rate	TD:3.00mm2	内部方法	1.5	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	0.60	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Friction coefficient vs. Metal5		SuzukiMethod	0.14
Friction coefficient 4			0.19
friction coefficient	-，对金属	ASTM D1894	0.14
friction coefficient	friction coefficient	-，对本身	ASTM D1894	0.19
Tensile stress	Yield,23°C	ISO527-2	90.0	Mpa
Tensile strain	Break,23°C	ISO527-2	4.0	%
Bending stress	23°C	ISO178	145	Mpa
IZOD notch impact strength	Notched，23℃	ASTM D256	130	J/m
	IZOD notch impact strength	Notched，-40℃	ASTM D256	100	J/m
		IZOD notch impact strength	Unnotched，-40℃	ASTM D256	40	KJ/m
		IZOD notch impact strength	IZOD notch impact strength	Unnotched，23℃	ASTM D256	60	KJ/m
elongation at break		ASTM D638/ISO 527	5	%
Tensile modulus	23°C	ISO527-2	5000	Mpa
tensile strength		ASTM D638/ISO 527	95	kg/cm²(MPa)[Lb/in²]
tensile strength	tensile strength	23℃	ASTM D638	95	Mpa
elongation	23℃	ASTM D638	5	%
Rockwell hardness		ASTM D785	89	M
Rockwell hardness	Rockwell hardness		ASTM D785	M89
Bending modulus		ASTM D790/ISO 178	4700	kg/cm²(MPa)[Lb/in²]
	Bending modulus	23°C	ISO178	4700	Mpa
	Bending modulus	Bending modulus	23℃	ASTM D790	4.7	GPa
bending strength	23℃	ASTM D790	125	Mpa
bending strength	bending strength		ASTM D790/ISO 178	125	kg/cm²(MPa)[Lb/in²]
IZOD notch impact strength		ASTM D256/ISO 179	130	kg·cm/cm(J/M)ft·lb/in
	IZOD notch impact strength		ASTM D256/ISO 179	100	kg·cm/cm(J/M)ft·lb/in
		IZOD notch impact strength		ASTM D256/ISO 179	60	kg·cm/cm(J/M)ft·lb/in
		IZOD notch impact strength	IZOD notch impact strength		ASTM D256/ISO 179	40	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	HB
Hot deformation temperature		ASTM D648/ISO 75	204	℃（℉）
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	220	°C
		Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	195	°C
			Hot deformation temperature	-，0.45MPa	ASTM D648	220	°C
			Hot deformation temperature	Hot deformation temperature	-，1.82Mpa	ASTM D648	204	°C
Linear expansion coefficient		ASTM D696/ISO 11359	5.5x10^-5	mm/mm.℃
Flame retardancy		UL94	HB
Coefficient of linear expansion		ASTM D696	5.5
Linear coefficient of thermal expansion	MD：-30to100°C	ISO11359-2	5.5E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the anti leakage trace index	CTI	UL746	PLC0
Voltage endurance		ASTM D149	22	MV/m
Dissipation factor 6	23°C,50Hz	IEC60250	1E-03
Dissipation factor 6	Dissipation factor 6	23°C,1MHz	IEC60250	0.020
Arc resistance 7		IEC60950	110	sec
Dielectric constant 5	23°C,50Hz	IEC60250	3.40
Dielectric constant 5	Dielectric constant 5	23°C,1kHz	IEC60250	3.50
Tangent value of dielectric loss	-，50Hz	ASTM D150	0.001
Tangent value of dielectric loss	Tangent value of dielectric loss	-，10	ASTM D150	0.02
Volume resistivity		ASTM 257	2.0
Arc resistance coefficient		ASTM D495	110	S
Dielectric constant		ASTM D150/IEC 60250	3.4
	Dielectric constant	-，50Hz	ASTM D150	3.4
	Dielectric constant	Dielectric constant	-，10	ASTM D150	3.5
Volume resistivity		ASTM D257/IEC 60093	2.0X10^14	Ω.cm
Volume resistivity	Volume resistivity		IEC60093	4E+16	ohms·cm
Dielectric strength		IEC60243-1	22	KV/mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	60	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale,23°C	ISO2039-2	64

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength8	250°C,1.00mm	内部方法	8.50	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.