PBT DURANEX® 5010N6 JAPAN POLYPLASTIC

Unit Price:
$4076 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow : 2.00 mm	内部方法	1.8	%
Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm	内部方法	1.9	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.080	%
Melt Volume flow Rate	250°C/2.16 kg	ISO 1133	20.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus		ISO 178	2600	Mpa
Flexural Stress		ISO 178	90.0	Mpa
Tensile Stress	Yield	ISO 527-2/50	55.0	Mpa
Tensile Strain	Yield	ISO 527-2/50	4.3	%
Tensile Strain	Tensile Strain	Break	ISO 527-2/50	50	%
Tensile Modulus		ISO 527-2/1	2800	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Annealed	ISO 75-2/B	165	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Annealed	ISO 75-2/A	77.0	°C
Linear thermal expansion coefficient	Flow : -30 to 35°C	ISO 11359-2	8.0E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -30 to 120°C	ISO 11359-2	1.2E-4	cm/cm/°C
		Linear thermal expansion coefficient	Flow : 35 to 120°C	ISO 11359-2	1.4E-4	cm/cm/°C
			Linear thermal expansion coefficient	Across Flow : -30 to 35°C	ISO 11359-2	8.8E-5	cm/cm/°C
				Linear thermal expansion coefficient	Across Flow : -30 to 120°C	ISO 11359-2	1.2E-4	cm/cm/°C
				Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 35 to 120°C	ISO 11359-2	1.5E-4	cm/cm/°C
Melting temperature		ISO 11357-3	224	°C
RTI	0.71 mm	UL 746	140	°C
RTI Imp	0.71 mm	UL 746	120	°C
RTI Elec	0.71 mm	UL 746	140	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1 MHz	IEC 60250	0.020
Comparative Tracking Index		UL 746	PLC 1
Dielectric Strength	1.00 mm	IEC 60243-1	21	KV/mm
Dielectric Strength	Dielectric Strength	2.00 mm	IEC 60243-1	18	KV/mm
Surface Resistivity		IEC 60093	1.0E+15	ohms
Dielectric Constant	1 MHz	IEC 60250	3.20
Volume Resistivity		IEC 60093	1.0E+16	ohms·cm

Injection	Test Result	Unit
Injection Pressure	20.0 到 150	Mpa
Injection Rate	中等偏快
Drying time - Hot air dryer	120	°C
Drying time - Hot air dryer	5.0 到 8.0	hr
Mold Temperature	60 到 80	°C
Rear Temperature	235	°C
Middle Temperature	240	°C
Front Temperature	250	°C
Nozzle Temperature	245	°C
Screw Speed	80 到 120	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO 179	120	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.71 mm	UL 94	V-0
	Flame Rating	1.6 mm	UL 94	V-0
	Flame Rating	Flame Rating	3.2 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.