Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ASTM D-955 | 1.3-2.0 | % |
glass fiber content | | Ash | 0 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | | ASTM D-638 | 4-6 | % |
Flexural strength | | ASTM D-790 | 900-1200 | kg/cm |
Tensile strength | | ASTM D-638 | 500-700 | kg/cm |
Tensile Modulus | | ASTM D-790 | 25000-35000 | kg/cm |
Tensile Strength | | ASTM D638/ISO 527 | 700 | kg/cm²(MPa)[Lb/in²] |
Rockwell Hardness | | ASTM D785 | 88 | |
Rockwell Hardness | | ASTM D-785 | 88 | M-scale |
Izod notch impact strength | | ASTM D256/ISO 179 | 2.5-3.5 | kg·cm/cm(J/M)ft·lb/in |
Izod Impact Strength | | ASTM D-256 | 2.5-3.5 | kg.cm/cm |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flame resistance | 0.75mm | UL 94 | V-0 | |
Deflection Temperature Under Load? | 4.6Kg/cm | ASTM D-648 | 165 | °C |
Deflection Temperature Under Load? | 18.6Kg/cm | ASTM D-648 | 65 | °C |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 65 | ℃(℉) |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 165 | ℃(℉) |
Melting Temperature | | DSC | 225 | °C |
Coefficient of Linear Thermal Expansion | | ASTM D-696 | 9 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor | 60Hz | ASTM D-150 | 3.2 | |
Insulation failure strength | | ASTM D-149 | 18 | KV/mm |
Surface Resistivity | | ASTM D257/IEC 60093 | >10 | Ω |
Surface Resistivity | | ASTM D-257 | >10 | Ω |
Dielectric Constant | | ASTM D150/IEC 60250 | 302 | |
Dielectric Constant | | ASTM D150/IEC 60250 | 0.001 | |
Arc Resistance | | ASTM D495/IEC 60112 | 120 | |
Arc Resistance | | ASTM D-495 | 120 | sec |
Volume Resistivity | | ASTM D-257 | >10 | Ω.cm |
Dielectric Constant | 60Hz | ASTM D-150 | 0.001 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM D-570 | 0.05 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.