PBT Toraycon® 1200M TORAY JAPAN
47
- Unit Price:
- $3662 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 224 | g/10min | |
| Density | ASTM D792/ISO 1183 | 1.315 |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 250°C/1.0kg | ISO1133 | 8.7 | g/10min |
| Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 16.0 | cm3/10min |
| Melt Volume flow Rate | cm | ISO 1133 | ||
| parent Viscosity | 0.5%OCP | 内部方法 | 1.23 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | % | ISO 527-1/-2 | ||
| Flexural Stress | ISO178 | 83.0 | Mpa | |
| Tensile Stress | ISO527-2 | 58.0 | Mpa | |
| Tensile Strain | Break | ISO527-2 | 120 | % |
| Tensile Strength | Yield | ASTMD638 | 54.0 | Mpa |
| Charpy Notched Impact Strength | KJ/m | ISO 179/1eA | 5.1 | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 120 | % | |
| Tensile Strength | ASTM D638/ISO 527 | 58 | kg/cm²(MPa)[Lb/in²] | |
| MPa | ISO 527-1/-2 | 58 | ||
| Tensile Elongation | Break | ASTMD638 | >150 | % |
| Flexural Modulus | ASTMD790 | 2500 | Mpa | |
| ASTM D790/ISO 178 | 2.4 | kg/cm²(MPa)[Lb/in²] | ||
| Gpa | ISO 178 | 2.4 | ||
| ISO178 | 2400 | Mpa | ||
| Flexural Strength | ASTMD790 | 82.0 | Mpa | |
| ASTM D790/ISO 178 | 83 | kg/cm²(MPa)[Lb/in²] | ||
| MPa | ISO 178 | 83 | ||
| Charpy impact strength | ASTM D256/ISO 179 | 5.1 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | 224 | °C | ||
| Flame retardancy | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.