Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23°C,24hr | ASTMD570 | 0.10 | % |
Melt Mass-Flow Rate | 210°C/5.0kg | ASTMD1238 | 15 | g/10min |
Melt Mass-Flow Rate | 250°C/2.16kg | ASTMD1238 | 20 | g/10min |
Modeling Shrinkage | MD:24hr | ASTMD955 | 1.1 | % |
Modeling Shrinkage | TD:24hr | ASTMD955 | 1.1 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTMD638 | 170 | % |
Tensile Strength | Break | ASTMD638 | 7.50 | Mpa |
Flexural Modulus | 100mmSpan | ASTMD790 | 50.0 | Mpa |
Flexural Modulus | | ISO178 | 40.0 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 8.00 | Mpa |
Tensile Strain | Break | ISO527-2/50 | 170 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Brittleness Temperature | | ASTMD746 | <-40.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1MHz | IEC60250 | 2E-03 | |
Relative Permittivity | 1MHz | IEC60250 | 2.50 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Electric strength | 2.00mm,inOil | IEC60243-1 | 25 | KV/mm |
Volume Resistivity | | ASTMD257 | 1.3E+16 | ohms·cm |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Tearing Strength | | ISO6383-1 | 16.0 | N/mm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A,30sec | ASTMD2240 | 78 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 24 | % |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 775 | °C |
UL flame retardant rating | 6.0mm | UL94 | V-0 | |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.