Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 250°C/2.16 kg | ISO 1133 | 1.8 | g/10 min |
| Melt Mass-Flow Rate | 260°C/5.0 kg | ISO 1133 | 11 | g/10 min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield | ISO 527-2/5 | 48.0 | Mpa |
| Tensile Strain | Break | ISO 527-2/5 | 52 | % |
| Flexural Modulus | | ISO 178 | 3670 | Mpa |
| Flexural Stress | | ISO 178 | 89.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 4.00 mm | ISO 75-2/B | 104 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 94.0 | °C |
| Vicat Softening Temperature | | ISO 306/B50 | 109 | °C |
| RTI | | UL 746 | 80.0 | °C |
| RTI Imp | | UL 746 | 80.0 | °C |
| RTI Elec | | UL 746 | 80.0 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 80 到 100 | °C |
| Suggested Max Moisture | | | 0.020 | % |
| Processing (Melt) Temp | | | 260 到 300 | °C |
| Mold Temperature | | | 60 到 80 | °C |
| Drying Time | | | 3.0 到 4.0 | hr |
| Rear Temperature | | | 260 到 270 | °C |
| Middle Temperature | | | 270 到 290 | °C |
| Front Temperature | | | 290 到 300 | °C |
| Nozzle Temperature | | | 270 到 290 | °C |
| Back Pressure | | | 0.981 到 3.92 | Mpa |
| Screw Speed | | | < 80 | rpm |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.75 mm | UL 94 | V-0 | |
| Flame Rating | 1.5 mm | UL 94 | V-0 | |
| Flame Rating | 3.0 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.