Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 250°C/10.0kg | ASTMD1238 | 6.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/50 | 10.0 | Mpa |
Tensile Strain | Break | ISO527-2/50 | 230 | % |
Flexural Modulus | 100mmSpan | ASTMD790 | 40.0 | Mpa |
Flexural Modulus | | ISO178 | 35.0 | Mpa |
Tensile Elongation | Break | CCP METHOD | 270 | % |
Tensile Elongation | Break4 | ASTMD638 | 250 | % |
Tensile Elongation | Break,113°C3 | CCP METHOD | 250 | % |
Tensile Strength | Break | CCP METHOD | 17.0 | Mpa |
Tensile Strength | Break2 | ASTMD638 | 10.0 | Mpa |
Tensile Strength | Break,113°C3 | CCP METHOD | 18.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Brittleness Temperature | | ASTMD746 | <-40.0 | °C |
HeatDeformation6 | 100°C | CCP METHOD | 20 | % |
UL Temperature Rating | | CCP METHOD | 80 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC60093 | 9E+15 | ohms·cm |
Comparative Tracking Index | | IEC60112 | 600 | V |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A,30sec | ASTMD2240 | 83 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 850 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 750 | °C |
VW-1 | | CCP METHOD | Pass | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.