PPO IUPIACE™ AH40-3001 MITSUBISHI ENGINEERING JAPAN

Unit Price:
$3719 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:3.20mm		0.50to0.70	%
Modeling Shrinkage	Modeling Shrinkage	MD:3.20mm		0.50to0.70	%
Moisture Absorption	Saturation,23°C	ISO62	0.070	%
Melt Volume flow Rate	300°C/2.16kg	ISO1133	17.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break	23°C	ISO527-2	34	%
Flexural Stress	23°C	ISO178	76.0	Mpa
Tensile Stress	Yield,23°C	ISO527-2	43.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2	3.2	%
Tensile Modulus	23°C	ISO527-2	2500	Mpa
Flexural Modulus	23°C	ISO178	2500	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	110	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	95.0	°C
Linear thermal expansion coefficient	MD	ISO11359-2	6.7E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	7.1E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	1.00mm	IEC60243-1	38	KV/mm
Dielectric Strength	Dielectric Strength	3.00mm	IEC60243-1	20	KV/mm
Surface Resistivity		IEC60093	2E+15	ohms
Volume Resistivity		IEC60093	3E+16	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179	150	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.