Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 250°C/5.0 kg | ASTM D1238 | 20 | g/10 min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | 100 mm Span | ASTM D790 | 160 | Mpa |
Flexural Modulus | -- | ISO 178 | 140 | Mpa |
Tensile Strength | Break 2 | UL 1581 | 18.0 | Mpa |
Tensile Strength | Break 3 | ASTM D638 | 16.0 | Mpa |
Tensile Strength | Break, 113°C 4 | UL 1581 | 21.0 | Mpa |
Tensile Strength | Break | ISO 527-2/50 | 15.0 | Mpa |
Tensile Strain | Yield | ISO 527-2/50 | 140 | % |
Tensile Strain | Break 2 | UL 1581 | 220 | % |
Tensile Strain | Break 3 | ASTM D638 | 170 | % |
Tensile Strain | Break, 113°C 5 | UL 1581 | 160 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Brittleness Temperature | | ASTM D746 | < -40.0 | °C |
UL Temperature Rating | | UL 1581 | 80 | °C |
Heat Deformation | 100°C | UL 1581 | 9.0 | % |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1 MHz | IEC 60250 | 4.0E-3 | |
Dielectric Strength | 2.00 mm, in Oil | IEC 60243-1 | 24 | KV/mm |
Relative Permittivity | 1 MHz | IEC 60250 | 2.90 | |
Comparative Tracking Index | | IEC 60112 | 600 | V |
Surface Resistivity | | ASTM D257 | 5.1E+15 | ohms |
Volume Resistivity | | ASTM D257 | 1.5E+15 | ohms·cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A, 30 sec | ASTM D2240 | 89 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 3.0 mm | IEC 60695-2-12 | 850 | °C |
Oxygen Index | | ISO 4589-2 | 27 | % |
Oxygen Index | VW-1 2 | UL 1581 | Pass | |
Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 750 | °C |
Flame Rating | 4.0 mm, Testing by SABIC | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.