PPO FLEX NORYL™ WCV072-111 SABIC INNOVATIVE SHANGHAI
105
- Unit Price:
- $4234 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Non enhanced Thermal stability
- Application Areas:Electronic and Electrical Automotive External Parts Car hood
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.12 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.050 | % | |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 14 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 13.4 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 3 | Yield | ASTMD638 | 15 | % |
| Tensile modulus 2 | ASTMD638 | 1710 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 43.8 | Mpa |
| Break | ASTMD638 | 41.5 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 1560 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 53.2 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 44.6 | Mpa |
| Break | ISO527-2/50 | 42.1 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 11 | % |
| Break | ISO527-2/50 | 46 | % | |
| Tensile modulus | ISO527-2/1 | 1760 | Mpa | |
| Bending strength 5,6 | ISO178 | 59.3 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 83 | % |
| Bending modulus 5 | ISO178 | 1750 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 98.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 92.0 | °C |
| Vicat softening temperature | ASTMD152510 | 114 | °C | |
| -- | ISO306/B50 | 114 | °C | |
| -- | ISO306/B120 | 117 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 8.5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 8.4E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 45.9 | J |
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 34 | kJ/m² |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 6.9 | kJ/m² |
| 23°C | ISO180/1A | 37 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.