PPO NORYL™ V0150B-701 SABIC INNOVATIVE JAPAN
80
- Unit Price:
- $5824 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Low water absorption Non enhanced Low temperature impact re
- Application Areas:Outdoor applications Solar junction box Shell
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.50to0.70 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.18 | % |
| 平衡,23°C,50%RH | ISO62 | 0.060 | % | |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 3.5 | g/10min |
| Density | ASTMD792 | 1.11 | g/cm³ | |
| ISO1183 | 1.11 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 35.0 | mg |
| Tensile Strength | 屈服 | ASTMD638 | 70.0 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 105 | Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 | Mpa |
| 屈服 | ISO527-2/50 | 70.0 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 10 | % |
| 屈服 | ISO527-2/50 | 4.0 | % | |
| Tensile Modulus | ASTMD638 | 2500 | Mpa | |
| ISO527-2/1 | 2500 | Mpa | ||
| Tensile Strength | Break | ASTMD638 | 60.0 | Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 | % |
| 断裂 | ASTMD638 | 7.0 | % | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2550 | Mpa |
| ISO178 | 2400 | Mpa | ||
| Flexural Strength | ISO178 | 110 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 135 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 130 | °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Vicat Softening Temperature | ASTMD152511 | 155 | °C | |
| -- | ISO306/A50 | 160 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 155 | °C | |
| Thermal Conductivity | ISO8302 | 0.27 | W/m/K | |
| RTI Str | UL746 | 115 | °C | |
| RTI Imp | UL746 | 105 | °C | |
| RTI Elec | UL746 | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 33 | KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 26 | KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 16 | KV/mm | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Comparative Tracking Index | IEC60112 | 250 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| 23°C | ISO179/1eA | 14 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 180 | J/m |
| 23°C | ASTMD256 | 330 | J/m | |
| -30°C | ISO180/1A | 5.0 | kJ/m² | |
| 23°C | ISO180/1A | 13 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 113 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Oxygen Index | ISO4589-2 | 32 | % | |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 775 | °C |
| 2.0mm | IEC60695-2-13 | 775 | °C | |
| 3.0mm | IEC60695-2-13 | 775 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.