PPO NORYL™ HS2000X-80267 SABIC INNOVATIVE THAILAND
90
- Unit Price:
- $4503 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber mineral reinf
- Application Areas:medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 | % |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 7.6 | g/10min |
| 300°C/5.0kg | ASTMD1238 | 7.6 | g/10min | |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 6.80 | cm3/10min |
| 300°C/5.0kg | ISO1133 | 6.80 | cm3/10min | |
| Outdoor Suitability | UL746C | f1 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Yield | ASTMD638 | 74.0 | Mpa | |
| Break | ASTMD638 | 60.0 | Mpa | |
| yield | ISO527-2 | 71.7 | Mpa | |
| ASTMD638 | 3.8 | % | ||
| ISO527-2 | 3.7 | % | ||
| fracture | ISO527-2 | 57.1 | Mpa | |
| ISO527-2 | 11 | % | ||
| 50.0mm Span | ASTMD790 | 3670 | Mpa | |
| --1 | ASTMD638 | 3650 | Mpa | |
| Yield,100mm Span | ASTMD790 | 117 | Mpa | |
| Break,50.0mm Span | ASTMD790 | 117 | Mpa | |
| Break | ASTMD638 | 8.4 | % | |
| 100mm Span | ASTMD790 | 3550 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, Unannealed,6.40mm | ASTMD648 | 116 | °C | |
| 0.45MPa, Unannealed,6.40mm | ASTMD648 | 128 | °C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 126 | °C | |
| RTI | UL746 | 100 | °C | |
| RTIElec | UL746 | 100 | °C | |
| Evolution Calendar intelligent importer | UL746 | 85.0 | °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 108 | °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 117 | °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 111 | °C | |
| -- | ISO306/B50 | 132 | °C | |
| ISO306/B120 | 136 | °C | ||
| Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C |
| TD:-40to40°C | ASTME831 | 7.8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Hot-wire Ignition | HWI | UL746 | PLC0 | |
| High Amp Arc Ignition | HAI | UL746 | PLC2 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
| Dissipation Factor? | 1MHz | ASTMD150 | 4.4E-03 | |
| 50Hz | ASTMD150 | 0.017 | ||
| 60Hz | ASTMD150 | 0.017 | ||
| Surface Resistivity | ASTMD257 | >1.0E+16 | ohms | |
| Dielectric Constant | 50Hz | ASTMD150 | 2.89 | |
| 60Hz | ASTMD150 | 2.89 | ||
| 1MHz | ASTMD150 | 2.70 | ||
| Volume Resistivity | ASTMD257 | 1.2E+16 | ohms·cm | |
| Arc Resistance | ASTMD495 | PLC6 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C | ASTMD256 | 130 | J/m | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 443 | J |
| Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 810 | J/m |
| 23°C9 | ISO180/1A | 9.7 | kJ/m² | |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 2200 | J/m |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.47mm | UL94 | V-0 | |
| 2.01mm | UL94 | 5VA | ||
| RadiantPanelListing(UL) | UL94 | YES |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.