Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 0.80 | % |
Modeling Shrinkage | MD:3.00mm3 | 内部方法 | 0.20 | % |
PVLimit | vs.S45C | SuzukiMethod | 2.9 | MPa·m/s |
PVLimit | vs.SUS | SuzukiMethod | 2.0 | MPa·m/s |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
AmountofWear4 | vs.S45C | SuzukiMethod | 0.200 | mg/hr |
AmountofWear4 | vs.SUS | SuzukiMethod | 0.500 | mg/hr |
Flexural Modulus | 23°C | ISO178 | 9400 | Mpa |
Tensile Stress | 23°C | ISO527-2 | 110 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 1.5 | % |
Flexural Stress | 23°C | ISO178 | 156 | Mpa |
Coefficient of Friction | vs.S45C | SuzukiMethod | 0.15 | |
Coefficient of Friction | vs.SUS | SuzukiMethod | 0.060 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | ISO11359-2 | 2.1E-05 | cm/cm/°C |
Melting temperature | | DSC | 278 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC60093 | 10 | ohms·cm |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.