Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant Filler: Glass mineral 55% filler by weight
Application Areas:Electrical applications
Color:--
Grade:--

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm2	内部方法	0.75	%
	Shrinkage rate	MD:3.00mm4	内部方法	0.16	%
		Shrinkage rate	Flow	东丽法	0.15	%
		Shrinkage rate	Shrinkage rate	垂重方向	东丽法	0.55	%
Water absorption rate	23°C,24hr	ISO62	0.020	%
Flowing Long	320℃,98MPa,1mm厚	东丽法	110

Mechanical performance	Test Condition	Test Method	Test Result	Unit
abrasion		ASTM D-1044	70	mg/1000回
Tensile stress	Yield,23°C	ISO527-2	170	Mpa
Tensile strain	Break,23°C	ISO527-2	1.3	%
Bending stress	23°C	ISO178	255	Mpa
impact strength	Notched23℃	ASTM D-256	100	J/m
impact strength	impact strength	Unnotched23℃	ASTM D-256	25	KJ/m
tensile strength		ASTM D-638	1.3	%
Bending modulus	23°C	ISO178	18500	Mpa
bending strength		ASTM D-790	190	Mpa
hardness		ASTM D-785	122	洛氏
Fracture strength		ASTM D-732	65
Tensile strength		ASTM D-638	145	Mpa
friction coefficient	对钢	ASTM D-1894	0.28
Limit PV value		东丽法	815	KJ/m
Curved elastic body		ASTM D-790	15.1	GPa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Line expansion coefficient	Flow	ASTM D-696	1.7
Line expansion coefficient	Line expansion coefficient	垂重方向	ASTM D-696	2.5
Rongdian		DSC	278	°C
Hot deformation temperature	1.82MPa	ASTM D-648	>260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
Combustibility		UL-94	V-0
Linear coefficient of thermal expansion	MD	ISO11359-2	1.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	3E-05	cm/cm/°C
Melting temperature		ISO11357-3	278	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+16	ohms·cm
permittivity	10	ASTM D-150	5.0
Dielectric strength		IEC60243-1	22	KV/mm
Arc resistance W level		ASTM D-495	128	秒
Induced positive connection	10	ASTM D-150	0.002
Inherent resistance of volume		ASTM D-257	10	Ω.m
Insulation breakdown voltage		ASTM D-149	15	MV/m
DielectricConstant4	23°C,1MHz	IEC60250	4.90
Dissipation factor 4	23°C,1MHz	IEC60250	2E-03

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	30	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ISO2039-2	122

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.36mm	UL94	V-0

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate		ASTM D-570	0.02	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength5	320°C,1.00mm	内部方法	115	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.