Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 0.50 到 0.80 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.30 到 0.70 | % |
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.020 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO 527-2/1A/5 | 165 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 1.9 | % |
Tensile Modulus | | ISO 527-2/1A | 12200 | Mpa |
Flexural Modulus | 23°C | ISO 178 | 12000 | Mpa |
Flexural Stress | | ISO 178 | 255 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 2.9E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 6.2E-5 | cm/cm/°C |
Melting temperature | | ISO 11357-3 | 280 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 265 | °C |
Deflection Temperature Under Load? | 8.0 MPa, Unannealed | ISO 75-2/C | 205 | °C |
Glass Transition Temperature | | ISO 11357-2 | 90.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | > 1.0E+15 | ohms |
Volume Resistivity | | IEC 60093 | > 1.0E+15 | ohms·cm |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 100 到 110 | °C |
Suggested Max Moisture | | | 0.020 | % |
Processing (Melt) Temp | | | 330 到 340 | °C |
Mold Temperature | | | 140 到 160 | °C |
Drying Time | | | 3.0 到 4.0 | hr |
Rear Temperature | | | 290 到 300 | °C |
Middle Temperature | | | 310 到 320 | °C |
Front Temperature | | | 330 到 340 | °C |
Nozzle Temperature | | | 310 到 330 | °C |
Back Pressure | | | < 3.00 | Mpa |
Hopper Temperature | | | 20 到 30 | °C |
Injection Rate | | | 快速 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 42 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 42 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M -Sale | ISO 2039-2 | 100 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.38 mm | UL 94 | V-0 | |
Flame Rating | 1.5 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.