PPS FORTRON® 1342L4 CELANESE USA

Unit Price:
$6233 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
27MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	0.20到0.30	%
	Modeling Shrinkage	TD	ASTMD955	0.50到0.70	%
		Modeling Shrinkage	TD	ISO294-4	0.50	%
		Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.20	%
Moisture Absorption	饱和,23°C	ISO62	0.020	%
Density	--	ASTMD792	1.70	g/cm³
Density	Density	--	ISO1183	1.69	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	245	Mpa
Tensile Modulus		ISO527-2/1A/1	14400	Mpa
Tensile Elongation	断裂	ISO527-2/1A/5	1.6	%
Tensile Elongation	Tensile Elongation	断裂,23°C	ASTMD638	2.0	%
Flexural Modulus	23°C	ISO178	13700	Mpa
Tensile Strength	断裂	ISO527-2/1A/5	165	Mpa
Tensile Strength	Tensile Strength	断裂,23°C	ASTMD638	152	Mpa
Specific Wear Rate	416Stainless:32°C	ASTMD3702	166	10^-10in³·min/ft·lb·hr
	Specific Wear Rate	C-1018Steel:49°C	ASTMD3702	323	10^-10in³·min/ft·lb·hr
	Specific Wear Rate	Specific Wear Rate	C-1018Steel:93°C	ASTMD3702	825	10^-10in³·min/ft·lb·hr

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD	ISO11359-2	2.2E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	4E-05	cm/cm/°C
Melting temperature		ISO11357-3	280	°C
Deflection Temperature Under Load?	1.8MPa,未退火	ASTMD648	268	°C
	Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	270	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0MPa,未退火	ISO75-2/C	215	°C
Glass Transition Temperature		ISO11357-2	90.0	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	8.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.5	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	8.5	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	8.5	kJ/m²
Charpy Unnotched Impact Strength	23°C	ISO179/1eU	44	kJ/m²

Supplementary information	Test Condition	Test Method	Test Result	Unit
SpecimenThickness-Shrinkage		内部方法	3.18	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.