PPS FORTRON® 1140L7 SD3002 CELANESE USA
100
- Unit Price:
- $4974 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 100MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced High temperature resistan
- Application Areas:Fitness equipment fibre
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 0.50 到 0.70 | % |
| 流量 | ISO 294-4 | 0.10 到 0.30 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.020 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO 527-2/1A/5 | 170 | Mpa |
| Tensile Strain | Break | ISO 527-2/1A/5 | 1.6 | % |
| Flexural Stress | ISO 178 | 260 | Mpa | |
| Tensile Modulus | ISO 527-2/1A | 14500 | Mpa | |
| Flexural Modulus | 23°C | ISO 178 | 14500 | Mpa |
| Compressive Modulus | ISO 604 | 14000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 270 | °C |
| 8.0 MPa, Unannealed | ISO 75-2/C | 200 | °C | |
| Glass Transition Temperature | ISO 11357-2 | 90.0 | °C | |
| Melting Temperature | ISO 11357-3 | 280 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dielectric Strength | IEC 60243-1 | 26 | KV/mm | |
| Comparative Tracking Index | IEC 60112 | 125 | V |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 130 到 140 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 330 到 340 | °C | ||
| Mold Temperature | 140 到 160 | °C | ||
| Drying Time | 3.0 到 4.0 | hr | ||
| Rear Temperature | 290 到 300 | °C | ||
| Middle Temperature | 310 到 320 | °C | ||
| Front Temperature | 330 到 340 | °C | ||
| Nozzle Temperature | 310 到 330 | °C | ||
| Back Pressure | < 3.00 | Mpa | ||
| Hopper Temperature | 20 到 30 | °C | ||
| Injection Rate | 快速 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M -Sale | ISO 2039-2 | 100 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.38 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.