Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 0.40到0.60 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.20到0.60 | % |
Modeling Shrinkage | MD | ASTMD955 | 0.20到0.30 | % |
Modeling Shrinkage | TD | ASTMD955 | 0.50到0.70 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.020 | % |
Modeling Shrinkage | | ISO 294-4 | 0.2-0.6 | % |
Specific Volume | | ASTMD792 | 0.611 | cm³/g |
Density / Specific Gravity | | ASTMD792,ISO1183 | 1.65 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 285 | Mpa |
IZOD Notch Impact Strength | | ISO 180/1A | 10 | kJ/m² |
Tensile Strength | Break,23°C | ASTMD638 | 200 | Mpa |
Tensile Strength | Break | ISO527-2/1A/5 | 195 | Mpa |
Tensile Modulus | | ISO 527 | 14700 | Mpa |
Tensile Modulus | -40°C | ASTMD638 | 14500 | Mpa |
Tensile Modulus | 75°C | ASTMD638 | 11900 | Mpa |
Tensile Modulus | 150°C | ASTMD638 | 4270 | Mpa |
Tensile Modulus | 200°C | ASTMD638 | 3240 | Mpa |
Tensile Modulus | -- | ISO527-2/1A/1 | 14700 | Mpa |
Tensile Strength | | ISO 527 | 195 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 1.7 | % |
Tensile Elongation | Break | ISO527-2/1A/5 | 1.9 | % |
Rockwell Hardness | | ASTM-D785 | 100 | R-Scale |
Flexural Modulus | 23°C | ISO178 | 14500 | Mpa |
Flexural Modulus | | ISO 178 | 14500 | Mpa |
Flexural Strength | | ISO 178 | 285 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.80Mpa | ISO 75-A | 270 | °C |
Deflection Temperature Under Load? | 0.45MPa,Annealed | ASTMD648 | 280 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 265 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 270 | °C |
Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 215 | °C |
Flame Rating | | UL94 | V-0 | |
Linear thermal expansion coefficient | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 4.2E-05 | cm/cm/°C |
Glass Transition Temperature | | ISO11357-2 | 90.0 | °C |
Melting Temperature | | ISO11357-3 | 280 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1MHz | IEC60250 | 6.2E-03 | |
Dissipation Factor? | 1kHz | ASTMD150 | 1E-03 | |
Dissipation Factor? | 1MHz | ASTMD150 | 1E-03 | |
Comparative Tracking Index | | IEC60112 | 125 | V |
Dielectric Strength | | IEC60243-1 | 28 | KV/mm |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Dielectric Constant | 1kHz | ASTMD150 | 3.50 | |
Dielectric Constant | 1MHz | ASTMD150 | 3.50 | |
Dielectric Constant | 1MHz | IEC60250 | 4.60 | |
Arc Resistance | | ASTMD495 | 134 | sec |
Volume Resistivity | -- | ASTMD257 | 1E+16 | ohms·cm |
Volume Resistivity | -- | IEC60093 | >1.0E+15 | ohms·cm |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
SpecificHeatCapacityofMelt | | 内部方法 | 1500 | J/kg/°C |
Optical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Filler Content | | | 40 | % |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 10 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 10 | kJ/m² |
Notched Izod impact strength | 23°C | ISO180/1U | 34 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 53 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 53 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 100 | |
Rockwell Hardness | M-Sale | ISO2039-2 | 100 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.38mm | UL94 | V-0 | |
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 3.0mm | UL94 | 5VA | |
Oxygen Index | | ISO4589-2 | 47 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM-D570 | 0.02 | % |
Density / Specific Gravity | | ISO 1183 | 1.65 | g/cm³ |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
SpecimenThickness-Shrinkage | | 内部方法 | 3.18 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.