Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.62 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.04 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23°C,24hr | ISO62 | 0.040 | % |
Modeling Shrinkage | Flow ,80℃×2mmt | | 0.4 | % |
Modeling Shrinkage | Across Flow ,80℃×2mmt | | 1.0 | % |
Melt Viscosity | 310°C,1000sec^-1 | ISO11443 | 200000 | mPa·s |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | | ISO 179/1eA | 2.5 | KJ/m |
Fracture strain | | ISO 527-1,2 | 1.7 | % |
Tensile Stress | | ISO527-2 | 125 | Mpa |
Tensile Strain | Break | ISO527-2 | 1.7 | % |
Flexural Stress | | ISO178 | 230 | Mpa |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 1.7 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 230 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638/ISO 527 | 125 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ISO 527-1,2 | 125 | Mpa |
Flexural Modulus | | ASTM D790/ISO 178 | 11,500 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO178 | 11500 | Mpa |
Flexural Modulus | | ISO 178 | 11500 | Mpa |
Flexural Strength | | ISO 178 | 230 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 210 | °C |
Melting Temperature | | | 210 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 2 | mm/mm.℃ |
Coefficient of Linear Thermal Expansion | Flow | ISO 11359-2 | 2 | |
Coefficient of Linear Thermal Expansion | Across Flow | | 4 | |
Linear thermal expansion coefficient | TD | 内部方法 | 4E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD | 内部方法 | 2E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 1.8MPa | ISO 75-1 | 210 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1KHz | IEC 60250 | 0.021 | |
Dielectric Strength | 1MHz | IEC 60250 | 0.096 | |
Dissipation Factor | 3mmt | IEC 60243-1 | 9 | KV/mm |
Comparative Tracking Index | | IEC 60112 | 150 | V |
Dissipation Factor? | 1kHz | IEC60250 | 0.020 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.10 | |
Dissipation Factor? | 耐电弧性 | IEC60250 | 116 | sec |
Dielectric Strength | 3.00mm | IEC60243-1 | 9.0 | KV/mm |
Relative Permittivity | 1kHz | IEC60250 | 7.60 | |
Relative Permittivity | 1MHz | IEC60250 | 6.40 | |
Comparative Tracking Index | | IEC60112 | 150 | V |
Surface Resistivity | | IEC 60093 | 1×10 | Ω |
Surface Resistivity | | ASTM D257/IEC 60093 | 7.6 | Ω |
Dielectric Constant | 1KHz | IEC 60250 | 7.6 | |
Dielectric Constant | 1MHz | IEC 60250 | 6.4 | |
Volume Resistivity | | ASTM D257/IEC 60093 | 9 x 1015 | Ω.cm |
Volume Resistivity | | IEC60093 | 9E+15 | ohms·cm |
Volume Resistivity | | IEC 60093 | 9×10 | Ω·cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ISO2039-2 | 100 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | V-0 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 310℃,1000/sec | ISO 11443 | 200 | Pa·s |
Moisture Absorption | 23℃,水中24hr | ISO 62 | 0.02 | % |
Density | | ISO 1183 | 1.62 | g/cm |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
Color Number | | | HF2000/HD9100 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.