PPS Torelina® A756M TORAY JAPAN

Unit Price:
$5890 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Antistatic Glass fiber and inorgani Filler: Glass mineral 65% filler by weight
Application Areas:Electrical tools Electrical components parts Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:3.00mm2	内部方法	0.60	%
Modeling Shrinkage	Modeling Shrinkage	MD:3.00mm4	内部方法	0.30	%
Moisture Absorption	23°C,24hr	ISO62	0.020	%
Modeling Shrinkage	Flow	TORAY	0.15	%
Modeling Shrinkage	Modeling Shrinkage	垂直	TORAY	0.60	%
Taber Abrasion Resistance		ASTM D-1044	70	mg/1000次
Coefficient of Friction		ASTM D-1894	0.25

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Compressive Strength		ASTM D-732	75
Shearing Strength	23°C	JISK7214	75.0	Mpa
Unnotched Izod Impact Strength		ASTM D-256	15	KJ/m
Coefficient of Friction			0.25
Tensile Elongation	23℃	ASTM D-638	1.6	%
IZOD Notch Impact Strength		ASTM D-256	80	J/m
Taber Abrasion Resistance	1000Cycles	ISO9352	70.0	mg
Tensile Stress	Yield,23°C	ISO527-2	110	Mpa
Tensile Strain	Break,23°C	ISO527-2	0.80	%
Flexural Stress	23°C	ISO178	195	Mpa
Tensile Strength		ASTM D-638	120	Mpa
Rockwell Hardness		ASTM D-785	122	R
Flexural Modulus	23℃	ASTM D-790	15.7	GPa
Flexural Modulus	Flexural Modulus	23°C	ISO178	19500	Mpa
Flexural Strength	23℃	ASTM D-790	145	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	260	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.82MPa	ASTM D-648	＞260	°C
Melting Temperature		DSC	278	°C
Linear thermal expansion coefficient	MD	ISO11359-2	2E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	2.8E-05	cm/cm/°C
Melting temperature		ISO11357-3	278	°C
Coefficient of Linear Thermal Expansion	Flow	ASTM D-696	2.4
Coefficient of Linear Thermal Expansion	Coefficient of Linear Thermal Expansion	垂直	ASTM D-696	2.9

Electrical performance	Test Method	Test Result	Unit
Volume Resistivity	ASTM D-257	10	Ω.m
Dielectric Strength	IEC60243-1	6.0	KV/mm
Volume Resistivity	IEC60093	1E+08	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179	15	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ISO2039-2	122

Other	Test Condition	Test Method	Test Result	Unit
流向	98MPa	TORAY	60
限定PV值		TORAY	815	KJ/m

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.6mm	UL94	V-0

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	23℃，24hr	ISO 11443-A	0.02	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
BarFlowLength5	320°C,1.00mm	内部方法	8.00	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.