Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.92 | |
| Modeling Shrinkage | | ASTM D955 | 0.25/0.75 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 平行 | | 0.25 | % |
| Modeling Shrinkage | 垂直 | | 0.75 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 1.3 | % |
| Tensile Strength | | ASTM D638/ISO 527 | 172 | kg/cm²(MPa)[Lb/in²] |
| Tensile Strength | | | 164 | Mpa |
| Tensile Elongation | Break | | 2.5 | % |
| Rockwell Hardness | | | 96 | |
| Rockwell Hardness | | ASTM D785 | 110 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 1.54*10^4 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | | 1.63×10 | Mpa |
| Flexural Strength | | ASTM D790/ISO 178 | 176 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | | 244 | Mpa |
| Notched Izod Impact Strength | | | 12 | KJ/m |
| Compressive Strength | | | 160 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Peak Melting Temperature | | | 288 | °C |
| Deflection Temperature Under Load? | | | 270 | °C |
| Flame retardancy | | UL-94 | V-0 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 1MHz | | 0.010 | |
| Dielectric Strength | | | 14 | KV/mm |
| Surface Resistivity | | | 3×10 | Ω |
| Dielectric Constant | 1MHz | | 5.0 | |
| Volume Resistivity | | | 8×10 | Ω.m |
| Comparative Tracking Index | | | 125 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | | 1.94 | g/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.