Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.51 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | | KJ/m | GB/T 1843-1996 | |
| Compressive Strength | | MPa | GB/T 1041-1992 | |
| Modeling Shrinkage | 料流方向 | % | GB/T 15585-1995 | |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 1.8 | % |
| Tensile Strength | | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] |
| Tensile Strength | | MPa | GB/T 1040-1992 | |
| Tensile Elongation | Break | % | GB/T 1040-1992 | |
| Rockwell Hardness | | ASTM D785 | 100 | |
| Rockwell Hardness | | hr | GB/T 9342-1988 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 1.15*100000 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | MPa | GB/T 9341-2000 | |
| Flexural Strength | | MPa | GB/T 9341-2000 | 172 |
| Flexural Strength | | ASTM D790/ISO 178 | 172 | kg/cm²(MPa)[Lb/in²] |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.81MPa | ℃ | GB/T 1634.2-2004 | |
| Melting Temperature | | | 281 | ℃（℉） |
| Melting Temperature | | ℃ | GB/T 4608-1984 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | Ω | GB/T 1410-1989 | |
| Dielectric Constant | | MHz | GB/T 1409-1988 | |
| Volume Resistivity | | Ω.M | GB/T 1410-1989 | |
| Dielectric Strength | | kV/mm | GB/T 1408.1-1999 | |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability | 垂直法 | 级 | GB/T 2408-1996 | FV-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.