Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.91 | |
| Modeling Shrinkage | | ASTM D955 | 0.25 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.05 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 0.8 | % |
| Tensile Strength | | ASTM D638/ISO 527 | 20 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ASTM D790/ISO 178 | 2.5 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 30 | kg/cm²(MPa)[Lb/in²] |
| Izod notch impact strength | | ASTM D256/ISO 179 | 1.2 | kg·cm/cm(J/M)ft·lb/in |
| Izod notch impact strength | | ASTM D256/ISO 179 | 4.5 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | V-0 | |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | >500 | ℃（℉） |
| Melting Temperature | | | 278 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | | ASTM D150/IEC 60250 | 4.0 | |
| Arc Resistance | | ISO 14782 | 167 | |
| Volume Resistivity | | ASTM D257/IEC 60093 | 1*10^15 | Ω.cm |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold Temperature | | | 130-150 | °C |
| Processing temperature | | | 260-280 | °C |
| Processing temperature | | | 290-310 | °C |
| Processing temperature | | | 300-320 | °C |
| Processing temperature | | | 280-300 | °C |
| Pressure | | | 40-50 | Mpa |
| Pressure | | | 80-130 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.