PPS PPS-hGR30 SICHUAN DEYANG

Unit Price:
$4511 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
11MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.55

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage		GB/T 15585-1995	0.0025	mm/mm

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength		GB/T 1843-1996	11.5	kJ/m²
Compressive Strength		GB/T 1041-1992	140	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	1.7	%
Tensile Strength		ASTM D638/ISO 527	142	kg/cm²(MPa)[Lb/in²]
Tensile Strength	Tensile Strength		GB/T 1040-1992	142	Mpa
Tensile Elongation	Break	GB/T 1040-1992	1.70	%
Rockwell Hardness		ASTM D785	100
Rockwell Hardness	Rockwell Hardness		GB/T 9342-1988	100	hr
Flexural Modulus		ASTM D790/ISO 178	1.1*100000	kg/cm²(MPa)[Lb/in²]
Flexural Modulus	Flexural Modulus		GB/T 1042-1992	1.1×104	Mpa
Flexural Strength		GB/T 1042-1992	180	Mpa
Flexural Strength	Flexural Strength		ASTM D790/ISO 178	180	kg/cm²(MPa)[Lb/in²]

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.80MPa	GB/T 1634-1979(1989)	267	°C
Melting Temperature			282	℃（℉）
Melting Temperature	Melting Temperature		GB/T 4608-1984	282	°C
Flammability	垂直法	GB/T 2408-1996	FV-0	级

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		GB/T 1410-1989	2.3×1015	Ω
Dielectric Constant	1MHz	GB/T 1409-1988	4
Volume Resistivity		GB/T 1410-1989	1.0×1015	Ω.m
Dielectric Strength		GB/T 1408.1-1999	18.56	KV/mm

Physical	Test Condition	Test Method	Test Result	Unit
Density		GB/T 1033-1986	1.55	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.