PPS LNP™ THERMOCOMP™ OFL-4036 SABIC INNOVATIVE US
95
- Unit Price:
- $5671 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35.7MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High heat resistance Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：24hr | ASTMD955 | 0.10to0.20 | % |
| TD：24hr | ASTMD955 | 0.60to0.80 | % | |
| TD:24hr | ISO294-4 | 0.30to0.48 | % | |
| MD:24hr | ISO294-4 | 0.13to0.18 | % | |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 1.2E-03 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.010 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO527-2/5 | 121 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 1.3 | % |
| Flexural Stress | ISO178 | 180 | Mpa | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.44 | |
| Static | ASTMD3702Modified | 0.35 | ||
| Specific Wear Rate | Ring | ASTMD3702Modified | 7.00to8.00 | 10^-10in^5-min/ft-lb-hr |
| Washer | ASTMD3702Modified | 52.5 | 10^-10in^5-min/ft-lb-hr | |
| Tensile Modulus | ASTMD638 | 12800 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 124 | Mpa |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 11600 | Mpa |
| Tensile Modulus | ISO527-2/1 | 12000 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 1.3 | % |
| Flexural Modulus | ISO178 | 11100 | Mpa | |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 178 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 257 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 278 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 278 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 264 | °C | |
| Linear thermal expansion coefficient | TD：-40to40°C | ASTME831 | 4.9E-05 | cm/cm/°C |
| TD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| MD：-30to30°C | ASTMD696 | 2.5E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 2.3E-5to5.0E-5 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 2.4E-05 | cm/cm/°C | |
| TD：-30to30°C | ASTMD696 | 3.4E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 3.40 | J |
| 23°C,TotalEnergy | ASTMD3763 | 11.8 | J | |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 2.30 | J | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 5.7 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 25 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.