Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.75 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.01 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | ISO 527-1,2 | 145 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 145 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790/ISO 178 | 16000 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO 178 | 16000 | Mpa |
Flexural Strength | | ISO 178 | 215 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 215 | kg/cm²(MPa)[Lb/in²] |
Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 | KJ/m |
Fracture strain | | ISO 527-1,2 | 1.2 | % |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 1.2 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | V-0 | |
Coefficient of Linear Thermal Expansion | Flow | ISO 11359-2 | 2 | |
Coefficient of Linear Thermal Expansion | Across Flow | | 3 | |
Deflection Temperature Under Load? | 1.8MPa | ISO 75-1 | 270 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1KHz | IEC 60250 | 0.002 | |
Dielectric Strength | 1MHz | IEC 60250 | 0.003 | |
Comparative Tracking Index | | IEC 60112 | 125 | V |
Dissipation Factor | 3mmt | IEC 60243-1 | 16 | KV/mm |
Surface Resistivity | | IEC 60093 | 3×10 | Ω |
Dielectric Constant | 1MHz | IEC 60250 | 4.7 | |
Dielectric Constant | 1KHz | IEC 60250 | 4.6 | |
Volume Resistivity | | IEC 60093 | 2×10 | Ω·cm |
Volume Resistivity | | ASTM D257/IEC 60093 | 2.0 x 10^16 | Ω.cm |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow ,80℃×2mmt | | 0.4 | % |
Modeling Shrinkage | Across Flow ,80℃×2mmt | | 0.6 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 1.75 | g/cm |
Moisture Absorption | 23℃,水中24hr | ISO 62 | 0.01 | % |
Melt Viscosity | 310℃、1000/sec | ISO 11443 | 260 | Pa·s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.