LCP ZENITE® 5244L BK CELANESE USA

Unit Price:
$6279 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ISO 1183	1.71	g/cm³
Modeling Shrinkage	流动	ISO 294-4	0.1	%
Modeling Shrinkage	Modeling Shrinkage	垂直	ISO 294-4	0.4	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23.0 °C	ISO 179/1eA	27	kJ/m²
Charpy Unnotched Impact Strength	23.0 °C	ISO 179/1eU	16.6	kJ/m²
Unnotched Izod Impact Strength	23.0 °C	ISO 180/1U	28.0	kJ/m²
Tensile Modulus		ISO 527-2/1A	14000	Mpa
Tensile Strength	断裂	ISO 527-2/1A	131	Mpa
Tensile Elongation	断裂	ISO 527-2/1A	1.66	%
Flexural Modulus		ISO 178	13100	Mpa
Flexural Strength		ISO 178	198	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa	ISO 75-1, -2	285	°C
Melting temperature	10°C/min	ISO 11357-1,-2,-3	318	°C
Coefficient of Linear Thermal Expansion	流动	ISO 11359-2	0.0000060	cm/cm/°C
Coefficient of Linear Thermal Expansion	Coefficient of Linear Thermal Expansion	垂直	ISO 11359-2	0.000048	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	2.05 GHz		4.18
Dissipation Factor?	2.05 GHz		0.004

Flame Rating	Test Condition	Test Method	Test Result	Unit
Fire rating	1.50 mm	UL94	V-0
Fire rating	Fire rating	0.800 mm	UL94	V-0

加工条件	Test Method	Test Result	Unit
Mold Temperature	cavity	80.0 - 120	°C
下料段温度		40.0 - 60.0	°C
第一段温度		320 - 330	°C
第二段温度		335 - 345	°C
第三段温度		335 - 345	°C
第四段温度		335 - 345	°C
Nozzle Temperature		335 - 345	°C
Processing (Melt) Temp		325 - 345	°C
Drying Temperature		>= 150	°C
Drying Time		3.00	hour
建议水分含量		<= 0.010	%
注塑压力		50.0 - 150	Mpa
Holding Pressure		50.0 - 150	Mpa
Back Pressure		<= 3.00	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.