Technical Data Sheet
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO 527-2/1A | 13000 | Mpa |
Flexural Modulus | 23°C | ISO 178 | 12700 | Mpa |
Tensile Stress | Break | ISO 527-2/1A/5 | 130 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 1.7 | % |
Flexural Stress | 23°C | ISO 178 | 170 | Mpa |
Flexural Strain (Break) | | ISO 178 | 1.9 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO 11357-3 | 328 | °C |
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 9.0E-6 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 3.8E-5 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 286 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 262 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | 1.0E+16 | ohms |
Volume Resistivity | | IEC 60093 | 1.0E+16 | ohms·cm |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 150 到 170 | °C |
Suggested Max Moisture | | | 0.010 | % |
Processing (Melt) Temp | | | 335 到 345 | °C |
Mold Temperature | | | 80 到 130 | °C |
Drying Time | | | 6.0 | hr |
Rear Temperature | | | 315 到 325 | °C |
Middle Temperature | | | 325 到 335 | °C |
Front Temperature | | | 330 到 350 | °C |
Nozzle Temperature | | | 330 到 340 | °C |
Injection Rate | | | 中等偏快 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 26 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.